Linear laser fast scanning thermography NDT for artificial disbond defects in thermal barrier coatings

Interface disbond in thermal barrier coatings (TBCs) is one of the key issues that cause their premature failure. In general, blind hole defects are often used as substitutes in transient thermography. The linear laser fast scanning thermography (LLFST) method was developed in this study and combined with several post-processing algorithms to accurately detect blind hole defects in TBCs. Through numerical simulation and experimental verification, a unique thermal response characteristic of blind holes in the cooling phase, namely a distinct "tailing" phenomenon, was summarized and utilized to recognize small defects. Validation tests indicated that blind holes with diameters of 1, 2, and 3 mm and artificial disbonds with diameters of 2 and 3 mm in TBCs are detected with high efficiency.