Dentin bond strength and nanoleakage of the adhesive interface after intracoronal bleaching

This study evaluated dentin bond strength (BS) and nanoleakage of non- and pre-etched dentin immediately (T₀ ,), 7 days (T₇ ), and 14 days (T₁₄ ) after bleaching. Bovine incisors (150) were selected and half of them submitted to intrapulpal dentin etching (e). Non- and pre-etched dentin were subjected to the following (n = 15): no bleaching/control (C); 35% carbamide peroxide (CP); 35% hydrogen peroxide (35% HP); 25% hydrogen peroxide (25% HP); and sodium perborate (SP). Bleaching agents were applied to the pulp chamber four times within a 72-h interval. Afterwards, pulp chamber dentin was prepared for the BS test at different evaluation times (n = 5): T₀ , T₇ , and T₁₄ . Composite blocks were built on pulp chamber and sectioned in slices. Slices were reduced to an hour-glass shape with a cross-sectional area of 0.8 mm² and submitted to microtensile BS test. Two additional specimens for each group were prepared for nanoleakage evaluation by transmission electron microscopy (TEM). Results were analyzed by ANOVA (two-way) and Dunnett's test (p < .05). BS decreased immediately after intracoronal bleaching for both sound and pre-etched dentin (p < .05). At T₁₄ , the BS of non-etched bleached dentin increased for all groups, whereas the pre-etched SPe group presented BS similar to the Ce. Nanoleakage within the hybrid layer was perceptible immediately after bleaching, although a decrease in nanoleakage was observed for all groups at T₁₄ . Adhesive restorations should be performed 7-14 days after bleaching, according to the bleaching agent used. Intracoronal bleaching should be performed preferably with sodium perborate if previous dentin etching is applied.