Hotspot relaxation time of NbN superconducting nanowire single-photon detectors on various substrates

Hotspot relaxation time (τ _th ) is one of the essential parameter which defines the maximum count rate of superconducting nanowire single-photon detectors (SNSPDs). We studied the τ _th for NbN-based SNSPDs on various substrates using the two-photon detection method based on the pump-probe spectroscopy technique. We observed that τ _th strongly increased with increasing bias current in the two-photon detection regime. In addition, the minimum hotspot relaxation time (τ _th )_min was not significantly affected by the bath temperature; this is different from the previous observations reported for WSi SNSPDs. In addition, a strong dependency of (τ _th )_min on the substrate was found. The minimum (τ _th )_min was 11.6 ps for SNSPDs made of 5.5-nm-thick NbN on MgO (100), whereas the maximum (τ _th )_min was 34.5 ps for SNSPDs made of 7.5-nm-thick NbN on Si (100). We presented a direct correlation between the values of τ _th and degrees of disorder of NbN films grown on different substrates.