Study on structure, mechanical property and cell cytocompatibility of electrospun collagen nanofibers crosslinked by...

Collagen electrospun scaffolds properly reproduce the framework of the extracellular matrix (ECM) of tissues that are natural with the fibrous morphology of the protein by coupling large biomimetism of the biological material. However, traditional solvents employed for collagen electrospinning lead to poor mechanical attributes and bad hydro-stability. In this work, by N-(3-dimethylaminopropyl)-N'-ethylcarbodiimide hydrochloride with N-hydroxysulfosuccinimide (EDC-NHS), glutaraldehyde (GTA) and genipin (GP) respectively, electrospun collagen fibers cross-linked, effectively stabilized the fiber morphology over 2months and improved the mechanical properties in both dry and wet state, especially EDC-NHS with large ultimate tensile stress and ε_b. The secondary structure of collagen structure still remained and had no obvious difference among various crosslinked samples according to FTIR. On the cell assessment, electrospun collagen fibers crosslinked by EDC-NHS, GTA and GP, were found to support cell adhesion, spreading and proliferation of MC3T3-E1. By contrast, GTA was more effective in preserving explicit fibrous morphology with a relatively lower cell viability both in FBS and BSA soaked mats. Interestingly, GP also had the similar cytocompatibility of MC3T3-E1 as EDC-NHS did. The study proved the feasibility of chemical crosslinker to electrospun collagen for biomedical application.