Polysiloxane/Polystyrene Thermo-Responsive and Self-Healing Polymer Network via Lewis Acid-Lewis Base Pair Formation

The use of thermo-reversible Lewis Pair (LP) interactions in the formation of transient polymer networks is still greatly underexplored. In this work, we describe the synthesis and characterization of polydimethylsiloxane/polystyrene (PDMS/PS) blends that form dynamic Lewis acid-Lewis base adducts resulting in reversible crosslinks. Linear PS containing 10 mol % of di-2-thienylboryl pendant groups randomly distributed was obtained in a two-step one-pot functionalization reaction from silyl-functionalized PS, while ditelechelic PDMS with pyridyl groups at the chain-termini was directly obtained via thiol-ene "click" chemistry from commercially available vinyl-terminated PDMS. The resulting soft gels, formed after mixing solutions containing the PDMS and PS polymers, behave at room temperature as elastomeric solid-like materials with very high viscosity (47,300 Pa·s). We applied rheological measurements to study the thermal and time dependence of the viscoelastic moduli, and also assessed the reprocessability and self-healing behavior of the dry gel.