Fabrication of ultrathin MIL-96(Al) films and study of CO₂ adsorption/desorption processes using quartz crystal...

This contribution reports the fabrication and characterization of ultrathin films of nanoparticles of the water stable microporous Al tricarboxylate metal organic framework MIL-96(Al). The preparation of MOF dispersions in chloroform has been optimized to obtain dense monolayer films of good quality, without nanoparticle agglomeration, at the air-water interface that can be deposited onto solid substrates of different nature without any previous substrate functionalization. The MOF studied shows great interest for CO₂ capture because it presents Al³⁺ Lewis centers and hydroxyl groups that strongly interact with CO₂ molecules. A comparative CO₂ adsorption study on drop-cast, Langmuir-Blodgett (LB) and Langmuir-Schaefer (LS) films using a Quartz Crystal Microbalance-based setup (QCM) has revealed that the CO₂ uptake depends strongly on the film fabrication procedure and the storage conditions. Noteworthy the CO₂ adsorption capacity of LB films is increased by 30% using a simple and green treatment (immersion of the film into water during 12 h just after film preparation). Finally, the stability of LB MOF monolayers upon several CO₂ adsorption/desorption cycles has been demonstrated, showing that CO₂ can be easily desorbed from the films at 303 K by flowing an inert gas (He). These results show that MOF LB monolayers can be of great interest for the development of MOF-based devices that require the use of very small MOF quantities, especially gas sensors.