Preparation and performance of crosslinked poly(arylene ether)s containing azobenzene chromophores
Yuxuan Zhang1, Shuang Wang1, Zhonghui Wang1
1Liaoning Key Laboratory for Green Synthesis and Preparative Chemistry of Advanced Materials, College of Chemistry, Liaoning University, Shenyang, China.
Abstract:
A series of novel poly(arylene ether)s with crosslinked groups and different azobenzene chromophores contents (azo-CPAEs: PAE-allyl20%-azo20%, PAE-allyl20%-azo40%, PAE-allyl20%-azo60%) were synthesized from a new bisfluoro monomer, (2,6-difluorophenyl)-(4-hydroxyphenyl)methanone. Their chemical structures were characterized by means of UV-vis and FI-IR. The thermal properties of the polymers were investigated by TGA and DSC, indicating the polymers had high glass transition temperatures (Tg > 147 °C) and good thermal stability (Td5 > 360 °C) even when the contents of azobenzene chromophores was high to 60%. And the influence of thermal crosslinking on the performance of PAE-allyl20%-azo20%, a typical one of the series, was investigated. Tg of PAE-allyl20%-azo20% increased with the increase of heating time when heat-treated at 250 °C for 20, 40 and 60 min, indicating the crosslink degree of the polymer increased. After heat-treated for 60 min, Tg of PAE-allyl20%-azo20% increased to 175 °C from 147 °C before thermal crosslinking. Upon irradiation with a 532 nm neodymium doped yttrium aluminum garnet (Nd:YAG) laser beam, the remnant value of the polymer PAE-allyl20%-azo20% before and after the thermal crosslinking were 81 and 96%, respectively, meaning that the PAE-allyl20%-azo20% after thermal crosslink showed more stable photoinduced alignment than that before thermal crosslinking.
More Related Videos
08:59A Freeze-Thawing Method to Prepare Chitosan-Polyvinyl alcohol Hydrogels Without Crosslinking Agents and Diflunisal Release Studies
Published on: January 14, 2020
08:51Preparation of Polypentafluorophenyl acrylate Functionalized SiO2 Beads for Protein Purification
Published on: November 19, 2018
Related Concept Videos
02:29Ethers from Alcohols: Alcohol Dehydration and Williamson Ether Synthesis
Ethers can be prepared from organic compounds by various methods. Some of them are discussed below,
Preparation of Ethers by Alcohol Dehydration
In this method, in the presence of protic acids, alcohol dehydrates to produce alkenes and ethers under different conditions. For example, in the presence of sulphuric acid, dehydration of ethanol at 413 K yields ethoxyethane, whereas it yields ethene at 443 K.
02:36Crown Ethers
02:28Structure and Nomenclature of Ethers
Ethers are organic compounds with an ether functional group which is characterized by an oxygen atom connected to two — identical or different — alkyl, aryl, or vinyl groups. The C–O–C linkage in dimethyl ether — the simplest ether — has an approximately tetrahedral bond angle of 110.3 degrees. The oxygen atom is sp3- hybridized, with the C–O distance being about 140 pm.
Classification of Ethers
Based on their attached substituent...
02:17Physical Properties of Ethers
An ether molecule has a net dipole moment due to the polarity of C–O bonds. Subsequently, boiling points of ethers are lower than those of alcohols of comparable molecular weight and slightly higher than those of hydrocarbons of comparable molecular weight (Table 1).
Ethers can act as hydrogen bond acceptors, making them more water-soluble than hydrocarbons, but since ethers cannot act as hydrogen bond donors, they are much less soluble in water than alcohols. Ethers are considered...
02:23Autoxidation of Ethers to Peroxides and Hydroperoxides
02:18Ethers to Alkyl Halides: Acidic Cleavage