Enhanced bone regeneration composite scaffolds of PLLA/β-TCP matrix grafted with gelatin and HAp

The composite polylactide PLLA/β-TCP scaffolds were fabricated by solution casting and were coated with gelatin/hydroxyapatite (Gel/HAp) to improve the biological properties of the composite scaffolds. The Gel/HAp mixture was prepared using an in situ reaction, and a grafting-coating method was used to increase the efficiency of coating the PLLA/β-TCP matrix with Gel/HAp. First, free amino groups were introduced by 1,6-hexanediamine to aminolyze the PLLA/β-TCP matrix surface. Second, glutaraldehyde was coupled to Gel/HAp as a crosslinking agent. The structure and properties of Gel/HAp-modified PLLA/β-TCP films were characterized by Fourier transform infrared spectroscopy (FT-IR), differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and water contact angle measurements (WCA). The experimental results show that 23 wt% HAp was uniformly dispersed in the gelatin coating by in situ synthesis. The Gel/HAp composite coating was successfully immobilized on the aminolyzed PLLA/β-TCP surface via a chemical grafting method, which promoted a lower degradation rate and was more hydrophilic than a physical grafting method. The Gel/HAp composite coating adhered tightly and homogeneously to the hydrophobic PLLA/β-TCP surface. Moreover, mouse embryo osteoblast precursor (MC3T3-E1) cells grown on the scaffolds were behaviorally and morphologically characterized. The results indicated that the Gel/HAp composite coating was favorable for the attachment and proliferation of preosteoblasts and that Gel/HAp-NH-PLLA/β-TCP would be a candidate scaffold for bone repair.