Improving surface wettability and lubrication of polyetheretherketone (PEEK) by combining with polyvinyl alcohol
Xiaoduo Zhao1, Dangsheng Xiong1, Yuntong Liu1
1School of Materials Science and Engineering, Nanjing University of Science and Technology, 210094 Nanjing, China; Jiangsu Key Laboratory of Advanced Micro/Nano Materials and Technology, 210094 Nanjing, China.
Abstract:
Poor surface wettability and relative high friction coefficients of pristine polyetheretherketone (PEEK) have limited its application in orthopedic implants. In this study, inspired by the structure of natural articular cartilage, we presented a novel method to fabricate a "soft-on-hard" structure on the surface of pristine PEEK specimens, which combined a soft polyvinyl alcohol (PVA) hydrogel layer and a three-dimensional porous layer with PEEK substrates. A variety of analytical methods were used to evaluate their properties, our results demonstrated that the hydrogel layer could be seamlessly connected with substrate, and the hydrogel-covered PEEK owned a highly hydrophilic surface, a very low water contact angle of 7° could be obtained. The friction coefficients of untreated and hydrogel-covered PEEK surfaces were measured using a tribometer under water lubrication, due to the presence of the top hydrogel layer and the hard substrate could provide excellent aqueous lubrication and bearing capacity, respectively, the friction coefficient could be reduced from 0.292 to 0.021. In addition, the porous layer under PVA hydrogel layer could work as gel reservoirs, the reserved hydrogel would be released after the surface layer was sheared off, and a regenerable lubrication status was obtained. This work provides a new route for the design of improving the surface wettability and tribological properties of PEEK.
Related Concept Videos
01:23Design Example: Deciding Thickness of Lubricating Fluid in a Shaft
To calculate the required thickness of the lubricant layer, the tangential velocity at the shaft's surface must first be determined. This velocity is calculated by converting the rotational speed to angular velocity...
02:37Oxidation of Alcohols
The process of oxidation in a chemical reaction is observed in any of the three forms:
02:29Ethers from Alcohols: Alcohol Dehydration and Williamson Ether Synthesis
Ethers can be prepared from organic compounds by various methods. Some of them are discussed below,
Preparation of Ethers by Alcohol Dehydration
In this method, in the presence of protic acids, alcohol dehydrates to produce alkenes and ethers under different conditions. For example, in the presence of sulphuric acid, dehydration of ethanol at 413 K yields ethoxyethane, whereas it yields ethene at 443 K.
02:31Protection of Alcohols
Protection
It defines a protecting group as the masking agent to make the more reactive species inert to a given set of conditions. This concept is depicted via the illustration of liquid flow through different outlets in an assembly of pipes. The analogy helps to understand the role...
01:16Surface Tension and Surface Energy
Consider a beaker filled with liquid. The bulk molecules in the liquid experience equal attractive forces on all sides with the surrounding molecules. However, the surface molecules experience a net attractive force downward due to the bulk molecules. The surface of the liquid behaves like a stretched membrane,...
01:38Preparation of Alcohols via Substitution Reactions
Alcohols can be synthesized from alkyl halides via nucleophilic substitution reactions. The highly polar carbon-halogen bond in the substrate makes halide a good leaving group. The hydroxide ion or water can act as a nucleophile to take the place of halide and form an alcohol. The substitution reactions occur via two different reaction pathways, SN1 or SN2, depending on the nature of carbon attached to the halide.
Primary alcohols are synthesized from primary alkyl halides, and the...