Boosting Light Harvesting in Perovskite Solar Cells by Biomimetic Inverted Hemispherical Architectured Polymer Layer...

Biomimetic microarchitectured polymer layers, such as inverted hemispherical architectured (IHSA)-polydimethylsiloxane (PDMS) and hemispherical architectured (HSA)-PDMS layers, were prepared by a simple and cost-effective soft-imprinting lithography method via a hexagonal close-packed polystyrene microsphere array/silicon mold. The IHSA-PDMS/glass possessed superior antireflection (AR) characteristics with the highest/lowest average transmittance/reflectance ( T_avg/ R_avg) values of approximately 89.2%/6.4% compared to the HSA-PDMS/glass, flat-PDMS/glass, and bare glass ( T_avg/ R_avg ∼88.8%/7.5%, 87.5%/7.9%, and 87.3%/8.8%, respectively). In addition, the IHSA-PDMS/glass also exhibited a relatively strong light-scattering property with the higher average haze ratio ( H_avg) of ∼38% than those of the bare glass, flat-PDMS/glass, and HSA-PDMS/glass (i.e., H_avg ≈ 1.1, 1.7, and 34.2%, respectively). At last, to demonstrate the practical feasibility under light control of the solar cells, the IHSA-PDMS was laminated onto the glass substrates of perovskite solar cells (PSCs) as an AR layer, and their device performances were explored. Consequently, the short-circuit current density of the PSCs integrated with the IHSA-PDMS AR layer was improved by ∼17% when compared with the device without AR layer, resulting in the power conversion efficiency (PCE) up to 19%. Therefore, the IHSA-PDMS is expected to be applied as an AR layer for solar cells to enhance their light absorption as well as the PCE.