Effect of different irrigations on the bond strength of self-adhesive resin cement to root dentin
Carlos Garcia1, Edwin Ruales-Carrera2, Luiz-Henrique-Maykot Prates3
1DDS, MSc, Department of Dentistry, Federal University of Santa Catarina (UFSC), Florianópolis, SC, Brazil.
Background:
Different disinfectant solutions or medications are indicated prior fiber post bonding procedures.The aim was to evaluate the effect of different pretreatments of root canal on the bond strength of a fiber post luted to dentin with self-adhesive resin cement.
Material And Methods:
Forty-eight single-rooted mandibular premolars were endodontically treated and prepared to receive fiber posts. Teeth were assigned to four groups (n=12). Root canal walls were subjected to no pretreatment (G1 - control); irrigation with 10 mL of 5% sodium hypochlorite (NaOCl) (G2); 10 mL of 17% ethylenediaminetetraacetic acid (EDTA) associated with 10 mL of 5% NaOCl (G3); or 10 mL of 17% EDTA (G4). Fiber posts were bonded with self-adhesive cement. After the roots were sectioned into slices, a push-out bond strength test was performed using a universal testing machine at crosshead speed of 0.5 mm/min. Bond strength data were recorded and expressed in MPa and analyzed by Anova (5%) and Tukey Test (5%).
Results:
It was found that G2 (9.36 MPa) and G4 (6.33 MPa) were significantly different among themselves and statistically inferior to G1 (13.93 MPa) while G3 (14.31 MPa) was statistically similar to G1 (control) and superior to G2 and G4.
Conclusions:
Irrigation with 17% EDTA associated with 5% NaOCl showed increased bond strength compared with the same solutions used alone. Key words:Self-adhesive, Dentin, Push-out, Bonding.
More Related Videos
Related Concept Videos
01:20Strength of Cement
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
01:12Bonding and Strength of Aggregate
00:42Ionic Bonds
When atoms gain or lose electrons to achieve a more stable electron configuration they form ions. Ionic bonds are electrostatic attractions between ions with opposite charges. Ionic compounds are rigid and brittle when solid and may dissociate into their constituent ions in water. Covalent compounds, by contrast, remain intact unless a chemical reaction breaks them.
Opposing Charges Hold Ions Together in Ionic Compounds
Ionic bonds are reversible electrostatic interactions between ions...
02:49Bond Energies and Bond Lengths
01:14Adhesion
Capillary action is a result of water’s adhesive tendencies. When a narrow...
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...