Influence of pH on wet-synthesis of silver decorated hydroxyapatite nanopowder

Here, effect of solution pH on precipitation of silver decorated hydroxyapatite (Ag-HAp) nano powder during its wet-synthesis was systematically studied. XRD pattern of Ag-HAp nano powder synthesised at pH ranging from 5 to 10 shows that calcium hydrogen phosphate was formed as dominating phase when the solution pH was between 5 and 9 and this phase was gradually transformed into a stable HAp above pH 9. A quantitative analysis of silver amount in Ag-HAp nano powder synthesised at different pH showed that silver can be precipitated to its maximum amount at pH 8 and the further addition of ammonia leads to the formation of a silver-ammonium complex, thereby remaining in the solution. HR-TEM and XPS analysis further confirmed the presence of silver in HAp nanocrystals, synthesised at an optimum pH 9. This trace amount of silver in HAp nano powder showed effective antibacterial activity against Staphylococcus aureus and Escherichia coli. In addition, the cytocompatibility studies carried out on MG63 cells further confirmed the present optimised silver concentration of the Ag-HAp nano powder is well within the toxic limit to be useful in various biomedical applications.