[PREPARATION AND BIOCOMPATIBILITY OF IN SITU CROSSLINKING HYALURONIC ACID HYDROGEL]
Jiabi Liang1,2, Jun Li2, Ting Wang2
1Pharmaceutical Department, the Fifth Affiliated Hospital, Sun Yat-sen University, Zhuhai Guangdong, 519000, P.R.China.
Objective:
To fabricate in situ crosslinking hyaluronic acid hydrogel and evaluate its biocompatibility in vitro.
Methods:
The acrylic acid chloride and polyethylene glycol were added to prepare crosslinking agent polyethylene glycol acrylate (PEGDA), and the molecular structure of PEGDA was analyzed by Flourier transformation infrared spectroscopy and 1H nuclear magnetic resonance spectroscopy. Hyaluronic acid hydrogel was chemically modified to prepare hyaluronic acid thiolation (HA-SH). And the degree of HA-SH was analyzed qualitatively and quantitatively by Ellman method. HA-SH solution in concentrations (W/V) of 0.5%, 1.0%, and 1.5% and PEGDA solution in concentrations (W/V) of 2%, 4%, and 6% were prepared with PBS. The two solutions were mixed in different ratios, and in situ crosslinking hyaluronic acid hydrogel was obtained; the crosslinking time was recorded. The cellular toxicity of in situ crosslinking hyaluronic acid hydrogel (1.5% HA-SH and 4% PEGDA mixed) was tested by L929 cells. Meanwhile, the biocompatibility of hydrogel was tested by co-cultured with human bone mesenchymal stem cells (hBMSCs).
Results:
Flourier transformation infrared spectroscopy showed that most hydroxyl groups were replaced by acrylate groups; 1H nuclear magnetic resonance spectroscopy showed 3 characteristic peaks of hydrogen representing acrylate and olefinic bond at 5-7 ppm. The thiolation yield of HA-SH was 65.4%. In situ crosslinking time of hyaluronic acid hydrogel was 2 to 70 minutes in the PEGDA concentrations of 2%-6% and HA-SH concentrations of 0.5%-1.5%. The hyaluronic acid hydrogel appeared to be transparent. The toxicity grade of leaching solution of hydrogel was grade 1. hBMSCs grew well and distributed evenly in hydrogel with a very high viability.
Conclusions:
In situ crosslinking hyaluronic acid hydrogel has low cytotoxicity, good biocompatibility, and controllable crosslinking time, so it could be used as a potential tissue engineered scaffold or repairing material for tissue regeneration.
More Related Videos
08:35Hyaluronic-Acid Based Hydrogels for 3-Dimensional Culture of Patient-Derived Glioblastoma Cells
Published on: August 24, 2018
08:59A Freeze-Thawing Method to Prepare Chitosan-Polyvinyl alcohol Hydrogels Without Crosslinking Agents and Diflunisal Release Studies
Published on: January 14, 2020
Related Concept Videos
01:07Preparation of Acid Anhydrides
The carboxylate ion acts as a nucleophile that attacks the carbonyl carbon of the acid chloride to form a tetrahedral intermediate. Subsequently, the re-formation of the carbonyl group with the loss of the chloride ion as a leaving group leads to the formation of an acid...
01:31Preparation of Carboxylic Acids: Overview
01:19Preparation of Carboxylic Acids: Hydrolysis of Nitriles
01:18Preparation of Aldehydes and Ketones from Carboxylic Acid Derivatives
Carboxylic acid derivatives like acid chlorides and esters are more easily reducible than the corresponding acids. The derivatives reduce in the presence of mild reducing agents to give aldehydes. Aldehydes can also be prepared by Rosenmund reduction, that is, the reduction of...
01:13Preparation of Carboxylic Acids: Carboxylation of Grignard Reagents
01:24Preparation of Aldehydes and Ketones from Nitriles and Carboxylic Acids
Reducing carboxylic acid derivatives like acyl chlorides (RCOCl), esters (RCO2R′), and nitriles (RCN) using milder aluminum hydride agents like lithium tri-tert-butoxyaluminum hydride [LiAlH(O-t-Bu)3] and diisobutylaluminum hydride [DIBAL-H]...