Minimization of polymerization shrinkage effects on composite resins by the control of irradiance during the
Gabriel Felipe Guimarães1, Edilmar Marcelino2, Ivana Cesarino1
1Univ. Estadual Paulista, Faculdade de Ciências Agronômicas, Departamento de Bioprocessos e Biotecnologia, Botucatu, SP, Brasil.
Introduction:
High levels of shrinkage stress caused by volumetric variations during the activation process are one of the main problems in the practical application of composite resins.
Objective:
The aim of this study is to reduce the shrinkage stress and minimize the effects caused by composite resin volumetric variation due to the photopolymerization. In this way, this work proposes a systematic study to determine the optimal dimming function to be applied to light curing processes.
Material And Methods:
The study was performed by applying mathematical techniques to the optimization of nonlinear objective functions. The effectiveness of the dimming function was evaluated by monitoring the polymerization shrinkage stress during the curing process of five brands/models of composites. This monitoring was performed on a universal testing machine using two steel bases coupled in the arms of the machine where the resin was inserted and polymerized. The quality of the composites cured by the proposed method was analyzed and compared with the conventional photoactivation method by experiments to determine their degree of conversion (DC). Absorbance measurements were performed using Fourier-transform infrared spectroscopy (FT-IR). A T-test was performed on DC results to compare the photoactivation techniques. We also used scanning electron microscopy (SEM) to analyze in-vitro the adhesion interface of the resin in human teeth.
Results:
Our results showed that the use of the optimal dimming function, named as exponential, resulted in the significant reduction of the shrinkage stress (~36.88% ±6.56 when compared with the conventional method) without affecting the DC (t=0.86, p-value=0.44). The SEM analyses show that the proposed process can minimize or even eliminate adhesion failures between the tooth and the resin in dental restorations.
Conclusion:
The results from this study can promote the improvement of the composite resin light curing process by the minimization of polymerization shrinkage effects, given an operational standardization of the photoactivation process.
More Related Videos
05:42Detection and Removal of Tooth-Colored Composite Resin Using the Fluorescence-Aided Identification Technique
Published on: July 27, 2022
07:33Biological Sample Preparation by High-pressure Freezing, Microwave-assisted Contrast Enhancement, and Minimal Resin Embedding for Volume Imaging
Published on: March 19, 2019
Related Concept Videos
01:15Introduction to Statistical Process Control
01:27Shrinkage in Concrete
When concrete is still in its plastic state, it can undergo a decrease in volume by about 1% of its absolute volume. This decrease is known as plastic shrinkage. It arises either...
01:21Drying Shrinkage
A portion of this drying shrinkage can be reversed; if the concrete is...
01:24Carbonation Shrinkage
The concrete's permeability is slightly reduced as calcium carbonate produced during the reaction fills its pores. Furthermore, its strength is slightly enhanced as the water released during the reaction...
03:35Classifying Matter by Composition
According to its composition, the matter can be classified into two broad categories — pure substances and mixtures.
A pure substance is a form of matter that has a constant composition throughout with uniform properties. For example, any sample of sucrose has the same composition and same physical properties, such as melting point, color, and sweetness, regardless of the source from which it is isolated.
A mixture is composed of two or...
01:16Olefin Metathesis Polymerization: Ring-Opening Metathesis Polymerization (ROMP)