Influence of material and surface treatment on composite repair shear bond strength
Pantelis Kouros1, Eugenia Koliniotou-Koumpia1, Maria Spyrou1
1Department of Operative Dentistry, Dental School, Aristotle University of Thessaloniki, Thessaloniki, Greece.
Objectives:
The aim of this study is to investigate the influence of the composite material and surface treatment to the bond strength when repairing an aged composite surface with new composite.
Materials And Methods:
One hundred and sixty resin blocks of methacrylate composite and silorane composite prepared and aged in artificial saliva for 6 months. Specimens treated either with a diamond bur (DB) or air abrasion (AA), conditioned with orthophosphoric acid (OA) or sodium hypochloride (SH) and repaired with methacrylate or silorane composite using the corresponding adhesive system. Repaired composites underwent thermocycling fatigue (×5000), and bond strength was measured at shear.
Results:
Methacrylate achieved the highest bond strengths as repair material, in all combinations (26.54-55.56 MPa). Silorane only reached 8.12 MPa when repairing silorane treated with DB and OA. For all other treatment combinations repairing with silorane led to pretest failures. The most susceptible to repair composites/surface treatment combination is when repairing methacrylate treated with AA and SH and methacrylate composite (55.56 MPa).
Conclusions:
Silorane composites are not suitable to be used when repairing an old composite restoration. The repair material is the most critical factor, while aged surface treatment has only a minor influence to the shear bond strength.
More Related Videos
11:47The Effect of Interfacial Chemical Bonding in TiO2-SiO2 Composites on Their Photocatalytic NOx Abatement Performance
Published on: July 4, 2017
08:40Ultrasonic Welding of Thermoplastic Composite Coupons for Mechanical Characterization of Welded Joints through Single Lap Shear Testing
Published on: February 11, 2016
Related Concept Videos
01:12Bonding and Strength of Aggregate
02:49Bond Energies and Bond Lengths
00:42Ionic Bonds
When atoms gain or lose electrons to achieve a more stable electron configuration they form ions. Ionic bonds are electrostatic attractions between ions with opposite charges. Ionic compounds are rigid and brittle when solid and may dissociate into their constituent ions in water. Covalent compounds, by contrast, remain intact unless a chemical reaction breaks them.
Opposing Charges Hold Ions Together in Ionic Compounds
Ionic bonds are reversible electrostatic interactions between ions...
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
02:43Peptide Bonds
02:25Overview of DNA Repair
Chemically...