Bond strength of resin cement to zirconia treated in pre-sintered stage
Kamal Ebeid1, Sebastian Wille2, Tarek Salah3
1Department of Prosthodontics, Propaedeutics and Dental Materials, School of Dentistry, Christian-Albrechts University at Kiel, Germany; Department of Fixed Prosthodontics, Faculty of Dentistry, Ain Shams University, Egypt.
Purpose:
Aim of this study was to evaluate the tensile bond strength (TBS) between resin cement and zirconia surface treated in different sintering stages.
Materials And Methods:
Eighty zirconia discs having final dimensions of 12 mm diameter and 3.2 mm thickness were milled then divided into three main groups according to the type of surface treatment performed (group 1: air abrasion using 50 µm Al2O3 particles, group 2: silica coating using Rocatec soft, and group 3: a control group receiving no surface treatment). Groups 1 and 2 were divided into two subgroups each according to the stage in which the surface treatment was performed (subgroup A; surface treatment performed in the pre-sintered stage and subgroup B; surface treatment performed in the post-sintered stage). Discs were later bonded to composite core materials using resin cement then tested for TBS either being subjected to 3 days of water storage or 150 days of water storage and 37,500 thermal cycles.
Results:
Long-term aging caused a significant decrease in TBS of all subgroups except the subgroup air-abraded in the post-sintered stage. After long-term aging, the group silica coated in the pre-sintered stage showed the significantly lowest TBS compared to all other groups. There was also no significant difference between the subgroups air-abraded and silica coated in the pre-sintered stage. All specimens in the control group debonded during long-term aging.
Significance:
Air-abrading zirconia with Al2O3 at a reduced pressure in the pre-sintered stage may result in durable bond strength to resin cement.
Related Concept Videos
01:20Strength of Cement
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
01:12Bonding and Strength of Aggregate
00:42Ionic Bonds
When atoms gain or lose electrons to achieve a more stable electron configuration they form ions. Ionic bonds are electrostatic attractions between ions with opposite charges. Ionic compounds are rigid and brittle when solid and may dissociate into their constituent ions in water. Covalent compounds, by contrast, remain intact unless a chemical reaction breaks them.
Opposing Charges Hold Ions Together in Ionic Compounds
Ionic bonds are reversible electrostatic interactions between ions...
02:49Bond Energies and Bond Lengths
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
02:43Peptide Bonds