Antimicrobial photodynamic active biomaterials for periodontal regeneration

Biomaterials for periodontal regeneration may have insufficient mechanical and antimicrobial properties or are difficult to apply under clinical conditions. The aim of the present study was to develop a polymeric bone grafting material of suitable physical appearance and antimicrobial photodynamic activity.

Two light curable biomaterials based on urethane dimethacrylate (BioM1) and a tri-armed oligoester-urethane methacrylate (BioM2) that additionally contained a mixture of β-tricalcium phosphate microparticles and 20wt% photosensitizer mTHPC (PS) were fabricated and analyzed by their compressive strength, flexural strength and modulus of elasticity. Cytotoxicity was observed by incubating eluates and in direct-contact to MC3T3-E1 cells. Antimicrobial activity was ascertained on Porphyromonas gingivalis and Enterococcus faecalis upon illumination with laser light (652nm, 1×100J/cm², 2×100J/cm²).

The compressive strength, flexural strength and elastic modulus were, respectively, 311.73MPa, 22.81MPa and 318.85MPa for BioM1+PS and 742.37MPa, 7.58MPa and 406.23MPa for BioM2+PS. Both materials did not show any cytotoxic behavior. Single laser-illumination (652nm) caused total suppression of P. gingivalis (BioM2+PS), while repeated irradiation reduced E. faecalis by 3.7 (BioM1+PS) and 3.1 (BioM2+PS) log-counts.

Both materials show excellent mechanical and cytocompatible properties. In addition, irradiation with 652nm induced significant bacterial suppression. The manufactured biomaterials might enable a more efficient cure of periodontal bone lesions. Due to the mechanical properties functional stability might be increased. Further, the materials are antimicrobial upon illumination with light that enables a trans-mucosal eradication of residual pathogens.