Influence of pre-heating and ceramic thickness on physical properties of luting agents
Michele O Lima1, Anderson Catelan2, Giselle M Marchi1
11 Department of Restorative Dentistry, State University of Campinas, Piracicaba, Brazil.
Purpose:
The objective of this in vitro study was to evaluate the influence of ceramic thickness and pre-heating of luting agents on their physical properties.
Materials And Methods:
The materials RelyX Arc, RelyX Ultimate, RelyX Veneer, and Filtek Z350 Flow were handled at different temperatures (23°C or 54°C), inserted into matrix, and photoactivated through ceramic disks (0.75 mm or 1.5 mm). The following tests were performed ( n=8): degree of conversion, Knoop Hardness, cross-link density, water sorption, solubility, and ultimate tensile strength. Data were analyzed using three-way analysis of variance and Tukey's test (α=0.05).
Results:
Regarding ceramic thickness, the thinnest ceramic resulted in higher values of Knoop Hardness ( p=0.027). The lowest temperature (23°C) resulted in a higher solubility ( p=0.0257), and water sorption ( p=0.0229) values. There was also statistical difference among the materials: RelyX Arc showed a higher degree of conversion and ultimate tensile strength, followed by RelyX Veneer, RelyX Ultimate, and Filtek Z350 Flow. For Knoop Hardness and cross-link density tests, RelyX Ultimate showed the highest values, followed by RelyX Arc, RelyX Veneer, and Filtek Z350 Flow. For water sorption and solubility, RelyX Veneer showed the highest values, followed by RelyX Arc, RelyX Ultimate, and Filtek Z350 Flow.
Conclusion:
Pre-heating interfered with water sorption and solubility, whereas ceramic thickness only affected Knoop Hardness; the physical properties of the materials are dependent on their composition.
More Related Videos
08:29Multi-material Ceramic-Based Components – Additive Manufacturing of Black-and-white Zirconia Components by Thermoplastic 3D-Printing (CerAM - T3DP)
Published on: January 7, 2019
06:53Additive Manufacturing of Functionally Graded Ceramic Materials by Stereolithography
Published on: January 25, 2019
Related Concept Videos
02:57Physical and Chemical Properties of Matter
02:19Physical Properties Affecting Solubility
As for any solution, the solubility of a gas in a liquid is affected by the attractive intermolecular forces between solute and solvent species. Unlike solid and liquid solutes, however, there is no solute-solute intermolecular attraction to overcome when a gaseous solute dissolves in a liquid solvent since the atoms or molecules comprising a gas are far separated and experience negligible interactions. Consequently, solute-solvent interactions are the sole...
01:26Physical Properties of Amines
02:33Physical Properties of Alkanes
02:17Physical Properties of Ethers
An ether molecule has a net dipole moment due to the polarity of C–O bonds. Subsequently, boiling points of ethers are lower than those of alcohols of comparable molecular weight and slightly higher than those of hydrocarbons of comparable molecular weight (Table 1).
Ethers can act as hydrogen bond acceptors, making them more water-soluble than hydrocarbons, but since ethers cannot act as hydrogen bond donors, they are much less soluble in water than alcohols. Ethers are considered...
01:18Urine: Physical and Chemical Properties
The concentration of these solutes varies, with urea being the most abundant nitrogenous waste product. Other solutes include sodium, chloride, potassium, phosphate,...