S-incorporated TiO₂ coatings grown by plasma electrolytic oxidation for reduction of Cr(VI)-EDTA with sunlight

The plasma electrolytic oxidation (PEO) technique was used to prepare photocatalytic S-TiO₂ coatings on Ti sheets; the incorporation of the S ions was possible from the electrolyte for modifying the structural and optics characteristics of the material. In this work, substrates of Ti (ASME SB-265 of 20 × 20 × 1 mm) were used in a PEO process in 10 min, using constant voltage pulses of 340 V with frequency of 1 kHz and duty cycles of 10% and of 30%. Solutions with H₂SO₄ (0.1 M) and CH₄N₂S (52 and 79 mM) were used as electrolytes. X-ray diffraction, scanning electron microscopy, and energy dispersive spectroscopy (EDS) were utilized to analyze the surface morphology, crystalline phase, and chemical composition of the samples. According to the results, the catalyst coatings had microporous structure and contained anatase-rutile TiO₂ nanocrystalline mixture, until 73.2% rutile and 26.8% anatase in the samples grown with 30% duty cycle and the lowest concentration of CH₄N₂S. From the EDS measurements, the incorporation of sulfur ions to the coatings was 0.08 wt%. 99.5% reduction efficiency of Cr(VI)-EDTA with sunlight was observed after 2 h; it was determined by diphenyl carbazide spectrophotometric method. These coatings have potential for effective sunlight heterogeneous photoreduction of this toxic, cumulative, and non-biodegradable heavy metal that contaminates the soil and water and is a serious risk to sustainability, ecosystems, and human health.