Performance evaluation of treating oil-containing restaurant wastewater in microbial fuel cell using in situ...

Most studies conducted nowadays to boost electrode performance in microbial fuel cell (MFC) have focused on carbonaceous materials. The titanium suboxides (Ti₄O₇, TS) are able to provide a new alternative for achieving better performance in MFC and have been tested and demonstrated in this study. The Ti₄O₇ electrode with high electrochemical activity was modified by graphene/polyaniline by the constant potential method. Electrogenic microorganisms were more conducive to adhere to the anode electrode due to the presence of graphene/polyaniline. The MFC reactor with polyaniline /graphene modified TS (TSGP) anode achieves the highest voltage with 980 mV, and produces a peak power density of 2073 mW/m², which is 2.9 and 12.7 times of those with the carbon cloth anode, respectively, at the 1000 Ω external resistance. In addition, this study evaluates the effects of anolyte conductivity, pH, and COD on the treatment of oil-containing restaurant wastewater (OCRW) in MFC using TSGP anode. The OCRW amended with 120 mS/cm obtains the lowest internal resistance (160.3 Ω). Increasing the anodic pH, gradually from acidic (pH 5.5) to alkaline conditions (pH 8.0), resulted in a gradual increase in maximum power density to 576.4 mW/m² and a decrease in internal cell resistance to 203.7 Ω. The MFC at the COD 1500 mg/L could obtain steady-state output voltage during 103 h while removing up to 65.2% of the COD of the OCRW.