Mild acids facilitate functional dentin remineralization under thermo-mechanical stimuli

To evaluate if mechanical and thermal cycling promote remineralization at the resin-dentin interface after bonding with three different adhesive approaches.

Dentin surfaces were subjected to three different treatments: demineralization (1) by 37% phosphoric acid followed by application of an etch-and-rinse dentin adhesive Single Bond (Adper Single Bond) (SB); (2) by 0.5 M ethylenediaminetetraacetic acid (EDTA) followed by SB; (3) application of a self-etch dentin adhesive: Clearfil-SEB (Clearfil SE Bond). Bonded interfaces were stored during 24 hours and then submitted for 3 months to: (1) storage at 37ºC, (2) load cycling, (3) thermocycling, and (4) thermo+load cycling. One section was extracted from each tooth, monthly. Resin-dentin interfaces were analyzed by AFM nano-indentation, Raman spectroscopy/cluster analysis and Masson's trichrome staining at 24 hours, 1, 2 and 3 months, to determine remineralization at the interface.

Thermo+load cycling promoted the highest biomimetic remineralization at the hybrid layer formed with EDTA+SB and Clearfil-SEB, at the 1 month time point. A narrow mineral-depleted zone was observed after thermo+load cycling with EDTA+ SB, and at those specimens bonded with Clearfil-SEB. Thermo+load cycling remineralized the dentin interface treated with EDTA+SB and Clearfil-SEB, after 1 month of study period, providing bioactivity and maturity of formed minerals.

In vitro challenging (thermo+load cycling) favors dentin remineralization at the resin-dentin bonded interfaces promoted with mild conditioning acids.