Related Experiment Video

Updated: Feb 7, 2026

Three-Dimensional Printing Guide Template Assisted Percutaneous Vertebroplasty PVP
05:39

Three-Dimensional Printing Guide Template Assisted Percutaneous Vertebroplasty PVP

Published on: October 17, 2019

8.2K

Bone cements for percutaneous vertebroplasty and balloon kyphoplasty: Current status and future developments

Zhiwei He1, Qingpan Zhai2, Muli Hu2

  • 1Department of Orthopaedics, The First Affiliated Hospital of Soochow University, Suzhou, Jiangsu, China.

Journal of Orthopaedic Translation
|July 24, 2018
PubMed

Keywords:
balloon kyphoplastybone cementfilling materialsosteoporotic vertebral compression fracturesvertebroplasty

More Related Videos

Author Spotlight: Improving Percutaneous Vertebroplasty Surgical Accuracy and Efficiency Through Advanced Puncture Techniques09:29

Author Spotlight: Improving Percutaneous Vertebroplasty Surgical Accuracy and Efficiency Through Advanced Puncture Techniques

Published on: August 9, 2024

621
Percutaneous Hepatic Perfusion PHP with Melphalan as a Treatment for Unresectable Metastases Confined to the Liver09:02

Percutaneous Hepatic Perfusion PHP with Melphalan as a Treatment for Unresectable Metastases Confined to the Liver

Published on: July 31, 2016

12.4K

Related Concept Videos

Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
953
Soundness of Cement01:17

Soundness of Cement

The soundness of cement refers to the ability of cement paste to retain its volume after setting. Unsound cement can lead to expansion and structural damage due to the presence of free lime, magnesia, and calcium sulfate. Free lime hydrates very slowly, expanding and causing unsoundness, which is difficult to detect because it intercrystallizes with other compounds. Magnesia also reacts with water, forming crystals that can disrupt the cement's structure. Calcium sulfate can create...
578
Portland Cement01:21

Portland Cement

Portland cement is the essential binding ingredient in concrete, made from finely ground materials including lime, iron, silica, and alumina. Lime is derived primarily from limestone, marble, marl, seashells, and clays, which also supply iron and alumina, while silica is sourced from sand, chalk, and bauxite. Contemporary manufacturing of Portland cement is a significant source of carbon dioxide emissions, prompting research into reducing its content in concrete through alternative...
691
Fineness of Cement01:15

Fineness of Cement

The fineness of cement directly influences the rate of hydration, as the hydration begins at the surface of the cement particles. In addition to hydration, the fineness of cement is vital for various properties of concrete including workability, gypsum requirement, and long-term behavior. The fineness of cement is represented in terms of the specific surface of cement which is typically measured in square meters per kilogram, with several methods available for this determination.
Direct...
522
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
506
Types of Cement I01:21

Types of Cement I

Portland cement comes in several types, each with distinct properties and applications based on their chemical composition and hydration characteristics:
Type I (Ordinary Portland Cement) is widely used for general construction where special properties are not required. It has moderate sulfate resistance and heat of hydration.
Type II (Modified Cement) offers moderate resistance to sulfate attack and a lower rate of heat development compared to Type I. It is suitable for structures in...