Graphene-Incorporated Biopolymeric Mixed-Matrix Membrane for Enhanced CO₂ Separation by Regulating the Support Pore...

The CO₂ separation performance by a membrane is influenced essentially by film thickness, temperature, moisture, and pressure. Pore formation on the active layer and pore clogging of the membrane support are critical factors that impedes the CO₂ separation performance. This study involves the development of a novel nanocomposite membrane (CS/SF/GNP) consisting of chitosan (CS), silk fibroin (SF), and graphene nanoparticles (GNP). The CS acts as the matrix, SF contributes to the CO₂ facilitated transport by its inherent amines as carriers, and GNP helped in counteracting the support pore blockage during the gas separation test. The positive effect of GNP in the CS/SF/GNP was further apparent in the CO₂ permeance inconsequential drop of ∼7% during the initial 12 h in the presence of moisture and pressure. The detailed characterizations including FESEM, AFM, and swelling were performed for the membranes. The effect of sweep water flow rate, temperature, and feed absolute pressure on CO₂ separation performance from binary gas were performed. The CS/SF/GNP membrane exhibited CO₂ permeance of 159 GPU and CO₂/N₂ selectivity of 93 at 90 °C and a feed absolute pressure of 2 bar having a sweep side water flow rate of 0.05 mL/min. Further, when CS/SF/GNP membrane was tested to separate CO₂ from ternary gas mixture (CO₂/N₂/H₂), it displayed excellent CO₂ permeance of 126 GPU and selectivity for CO₂/N₂ and CO₂/H₂ as 104 and 52, respectively. The TGA isotherm and XPS analysis of CS/SF/GNP membrane suggested a thermal stability of the prepared membrane that establishes its suitability for the gas permeation at different temperature.