[Remineralization of demineralized dentin induced by bioactive glass NovaMin]

To explore the remineralization effect of bioactive glass NovaMin on demineralized dentin specimens, and to study the physical and chemical properties of formed structure at dentin surface.
 Methods: One mm-thickness coronal dentin slices were soaked in ethylene diamine tetraacetic acid (EDTA) for 48 h to prepare the completely demineralized dentin specimens and they were divided into 2 groups: an artificial saliva group (control group) and a NovaMin powder group. The specimens were treated with artificial saliva or NovaMin powder for 2 min (2 times every day), and the interval was 8 hours. Then, the specimens were soaked in the remineralization solution. After 7 days, the scanning electron microscope (SEM), energy dispersive X-ray (EDX), attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR) and X-ray diffraction (XRD) were used to detect dentin morphology, the physical and chemical properties of the formed structure at dentin surface.
 Results: The results of SEM showed that a defined surface layer in the NovaMin powder group could be observed in the SEM imaging at the 7th day, which completely occluded dentinal tubules; the EDX, ATR-FTIR and XRD analysis found that the mineralized layer formed at dentin surface was mainly composed of calcium and phosphate elements, which was similar to the hydroxyapatite-like crystal. However, there were no materials formed at the dentin surface in the control group, and the dentinal tubules were still open.
 Conclusion: NovaMin can remineralize the demineralized dentin specimens and occlude the dentinal tubules in hydroxyapatite-like crystal structure.