Impact of Dentinal Tubule Orientation on Dentin Bond Strength
Jing Guo1,2, Li-Ping Wang3, Jia Zhu1,2
1Department of Oral Anatomy and Physiology, the Affiliated Stomatological Hospital of Nanchang University, Nanchang, 330006, China.
Abstract:
This study aimed to determine the impact of dentinal tubule orientation on dentin bond strength to provide a reference for clinical cavity preparation in resin-bonded restoration. Patients aged 13-16 years were selected, including 18 males and 21 females. Forty-eight human maxillary first premolars from orthodontic extractions were chosen to prepare the test models with the dentinal tubule orientations perpendicular and parallel to the bonding substrate. The test models in the vertical and parallel groups were divided into three groups: total-etching with 20% phosphoric acid, total-etching with 35% phosphoric acid and self-etching, with the dentinal tubule surfaces bonded with composite resin blocks in each group. After the standard test models of dentinal tubule-composite resin blocks were placed in distilled water and stored at 37°C for 24 h, shearing tests were performed using a universal material testing machine at a crosshead speed of 0.5 mm/min. The bond strength values in the vertical group were 19.33±1.59 MPa for the 20% phosphoric acid group, 21.39±2.34 MPa for the 35% phosphoric acid group, and 16.88±1.54 MPa for the self-etching group. The bond strength values in the parallel group were 24.53±1.99 MPa for the 20% phosphoric acid group, 25.16±2.88 MPa for the 35% phosphoric acid group, and 20.83±1.99 for the self-etching group. After using same total-etching adhesive, the shear bond strength of the parallel group was higher than that of the vertical group, and the difference was statistically significant (P<0.05). Regardless of vertical group or parallel group, the difference in the bond strength value between the total-etching groups and the self-etching group was statistically significant (P<0.05). It was concluded that the dentin bonding substrate which was parallel to the direction of the dentin tubule achieved an improved bond strength; the total-etching adhesives achieved higher bond strengths in dentin bond than the self-etching adhesives.
More Related Videos
07:42Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
Published on: December 20, 2024
07:06Isolation of Primary Human Proximal Tubule Epithelial Cells and Their Use in Creating a Microphysiological Model of the Renal Proximal Tubule
Published on: May 9, 2025
Related Concept Videos
01:12Bonding and Strength of Aggregate
01:21Impact Strength of Concrete
00:42Ionic Bonds
When atoms gain or lose electrons to achieve a more stable electron configuration they form ions. Ionic bonds are electrostatic attractions between ions with opposite charges. Ionic compounds are rigid and brittle when solid and may dissociate into their constituent ions in water. Covalent compounds, by contrast, remain intact unless a chemical reaction breaks them.
Opposing Charges Hold Ions Together in Ionic Compounds
Ionic bonds are reversible electrostatic interactions between ions...
02:49Bond Energies and Bond Lengths
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
02:43Peptide Bonds