[Application of biomimetic mineralized collagen bone graft material in rabbits posterolateral spinal fusion]

To investigate the bone repair and regeneration ability of biomimetic mineralized collagen bone graft material and autologous bone marrow in rabbit posterolateral spinal fusion model.

Twenty-seven 20-week-old male New Zealand white rabbits ［weighing (5.0±0.5) kg］ were used to establish the posterolateral spinal fusion model of L ₅ and L ₆ segments by stripping the transverse process and exposing cancellous bone with electric burr. The rabbits were randomly divided into 3 groups, 9 in each group. Groups A, B, and C were implanted 1.5 mL autologous iliac bone, 1.5 mL (30 mm×10 mm×5 mm) biomimetic mineralized collagen bone graft material, and 1.5 mL (30 mm×10 mm×5 mm) biomimetic mineralized collagen bone graft material and autologous bone marrow in each bone defect. At 4, 8, and 12 weeks after operation, the apparent hardness of the bone grafting area was observed by manipulation method, in order to evaluate bone graft fusion effects. Three animals were sacrificed in each group at each time point, the vertebral body specimens were excised and the bone defect repair and fusion were observed by X-ray films, and three-dimensional CT examination was performed to evaluate whether new bone was formed in the body. HE staining was performed at each time point to observe the formation of new bone and the repair and fusion of bone defects.

The manipulation test showed that bone graft fusion was not found in all groups at 4 weeks after operation; 3 (50.0%), 2 (33.3%), and 4 (66.7%) of groups A, B, and C reached bone graft fusion at 8 weeks after operation; 5 (83.3%), 4 (66.7%), and 5 (83.3%) of groups A, B, and C reached bone graft fusion at 12 weeks after operation; the fusion rate of group C was similar to that of group A, and all higher than that of group B. X-ray film observation showed that the fusion rate of group C at 8 and 12 weeks after operation was higher than that of group B, similar to group A. Three-dimensional CT observation showed that the effect of bone fusion in group C was better than that in group B, which was close to group A. HE staining observation showed that large area of mature lamellar bone coverage appeared in the bone graft area of groups A, B, and C at 12 weeks after operation, the material was completely degraded, and the marginal boundary of the host bone disappeared and tightly combined.

Biomimetic mineralized collagen bone graft material mixed with autologous bone marrow has good osteoinduction and osteogenesis guidance. Compared with biomimetic mineralized collagen bone graft material, it has better and faster osteogenesis effect, which is close to autologous bone transplantation.