Related Experiment Video

Updated: Feb 6, 2026

Composition and Properties of Aquafaba: Water Recovered from Commercially Canned Chickpeas
10:35

Composition and Properties of Aquafaba: Water Recovered from Commercially Canned Chickpeas

Published on: February 10, 2018

34.6K

Effects of a bleaching agent on properties of commercial glass-ionomer cements

Fernanda Lúcia Lago de Camargo1, Ailla Carla Lancellotti2, Adriano Fonseca de Lima3

  • 1Department of Restorative Dentistry, Integrated School of Carajás School of Dentistry, Redenção, PA, Brazil.

Restorative Dentistry & Endodontics
|August 24, 2018
PubMed
Abstract

Keywords:
Dental materialsGlass-ionomer cementTooth whitening agents

More Related Videos

Application of a Coupling Agent to Improve the Dielectric Properties of Polymer-Based Nanocomposites06:34

Application of a Coupling Agent to Improve the Dielectric Properties of Polymer-Based Nanocomposites

Published on: September 19, 2020

6.4K
Preparation and In Vitro Characterization of Dendrimer-based Contrast Agents for Magnetic Resonance Imaging11:27

Preparation and In Vitro Characterization of Dendrimer-based Contrast Agents for Magnetic Resonance Imaging

Published on: December 4, 2016

10.6K

Related Concept Videos

Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
946
Soundness of Cement01:17

Soundness of Cement

The soundness of cement refers to the ability of cement paste to retain its volume after setting. Unsound cement can lead to expansion and structural damage due to the presence of free lime, magnesia, and calcium sulfate. Free lime hydrates very slowly, expanding and causing unsoundness, which is difficult to detect because it intercrystallizes with other compounds. Magnesia also reacts with water, forming crystals that can disrupt the cement's structure. Calcium sulfate can create...
574
The Looking Glass Self01:28

The Looking Glass Self

The concept of the looking-glass self describes how an individual's self-concept is shaped by their perception of how others see them. This psychological theory, first introduced by sociologist Charles Horton Cooley in 1902, posits that self-identity emerges in a social context and is influenced by the judgments—real or imagined—of others.Research suggests that individuals frequently overestimate how positively others perceive them. This is particularly evident in physical...
370
Portland Cement01:21

Portland Cement

Portland cement is the essential binding ingredient in concrete, made from finely ground materials including lime, iron, silica, and alumina. Lime is derived primarily from limestone, marble, marl, seashells, and clays, which also supply iron and alumina, while silica is sourced from sand, chalk, and bauxite. Contemporary manufacturing of Portland cement is a significant source of carbon dioxide emissions, prompting research into reducing its content in concrete through alternative...
691
Fineness of Cement01:15

Fineness of Cement

The fineness of cement directly influences the rate of hydration, as the hydration begins at the surface of the cement particles. In addition to hydration, the fineness of cement is vital for various properties of concrete including workability, gypsum requirement, and long-term behavior. The fineness of cement is represented in terms of the specific surface of cement which is typically measured in square meters per kilogram, with several methods available for this determination.
Direct...
520
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
504