The purpose of this study was to establish a clinically appropriate light-curing moment for resin composite cements while achieving the highest indirect tensile strength and lowest polymerization shrinkage.

Polymerization shrinkage of seven resin composite cements (Multilink Automix, Multilink Speed Cem, RelyX Ultimate, RelyX Unicem 2 Automix, Panavia V5, Panavia SA plus, VITA Adiva F-Cem) was measured at ambient temperatures of 23°C and 37°C. Testing was done for autopolymerized and light-cured specimens after light application at either 1, 5, or 10 minutes after mixing. Indirect tensile strength of all cements was measured after 24 hours of storage at temperatures of 23°C and 37°C, for autopolymerized and light-cured specimens after light application 1, 5, or 10 minutes after mixing. To illustrate filler size and microstructures, SEM images of all cements were captured. Statistical analysis was performed with one-way ANOVA followed by post hoc Fisher LSD test ( α=0.05).

Final polymerization shrinkage of the resin composite cements ranged from 3.2% to 7.0%. An increase in temperature from 23°C to 37°C as well as the light-curing moment resulted in material dependent effects on the polymerization shrinkage and indirect tensile strength of the cements. Polymerization shrinkage of the cements did not correlate with the indirect tensile strength of the cement in the respective groups. Highest indirect tensile strengths were observed for the materials containing a homogeneous distribution of fillers with a size of about 1 μm (Multilink Automix, Panavia V5, VITA Adiva F-Cem).

The magnitude of the effect of light-curing moment and temperature increase on polymerization shrinkage and indirect tensile strength of resin composite cements is material dependent and cannot be generalized.