Laboratory Study of Micro-shear Bond Strength of Two Resin Cements to Leucite Ceramics using Different Ceramic
Abdullah A Al-Harthi1, Mohammed H Aljoudi2, Mulham N Almaliki3
1Umm Al-Qura University, Makkah, Kingdom of Saudi Arabia, Phone: +966595066644,
Aim:
To evaluate the effect of Monobond Etch & Prime on the micro-shear bond strength (MSBS) of resin cements to leucite surface and to compare the MSBS of two different resin cements to conditioned leucite surfaces with different primer systems.
Materials And Methods:
Twenty-one leucite ceramic disks (10 mm diameter, 2 mm thickness) were divided into three groups (n = 7). Group I: 9.6% hydrofluoric (HF) acid and Monobond S (Ivoclar Vivadent, Liechtenstein), then conventional resin cement was applied. Group II: Monobond Etch & Prime (Ivoclar Vivadent, Liechtenstein), then conventional resin cement was applied. Group III: 9.6% HF acid and with Monobond N (Ivoclar Vivadent, Liechtenstein), then adhesive resin cement was applied. The assigned resin cement was applied in each disk through five plastic tubes with an inner diameter of 1.6 and 1.9 mm height, and then light cured. Micro-shear bond strength was determined by pulling out the resin cement using universal testing machine (Instron®, USA).
Results:
One-way analysis of variance (ANOVA) and Student's t-test were used to determine statistical difference (a = 0.05) between each two groups. The results showed that group III had the highest MSBS values (7.32 ± 2.47) followed by group II (6.24 ± 2.16), whereas group I had the lowest MSBS values (5.7 ± 2.7). Nevertheless, there was no statistically significant difference between the results of all the groups.
Conclusion:
Monobond Etch & Prime has shown comparable results to the most popular combination of HF acid and silane. The combination of HF acid and Monobond N and self-adhesive resin cement has shown the best MSBS results, though not statistically significant.
Clinical Significance:
The clinicians can use simplified ceramic primer technique (Monobond Etch & Prime) which has comparable MSBS to the most popular combination of HF acid and silane.
More Related Videos
Related Concept Videos
01:20Strength of Cement
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
01:12Bonding and Strength of Aggregate
00:42Ionic Bonds
When atoms gain or lose electrons to achieve a more stable electron configuration they form ions. Ionic bonds are electrostatic attractions between ions with opposite charges. Ionic compounds are rigid and brittle when solid and may dissociate into their constituent ions in water. Covalent compounds, by contrast, remain intact unless a chemical reaction breaks them.
Opposing Charges Hold Ions Together in Ionic Compounds
Ionic bonds are reversible electrostatic interactions between ions...
02:49Bond Energies and Bond Lengths
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...