Enhancement of the Mechanical Properties of Hydroxyapatite/Sulphonated Poly Ether Ether Ketone Treated Layer for
Roohollah Sharifi1, Davood Almasi2, Izman Bin Sudin3
1Department of Endodontics, School of Dentistry, Kermanshah University of Medical Sciences, Kermanshah, Iran.
Abstract:
The mechanical properties of coated layers are one of the important factors for the long-term success of orthopeadic and dental implants. In this study, the mechanical properties of the porous coated layer were examined via scratch and nanoindentation tests. The effect of compression load on the porous coated layer of sulphonated poly ether ether ketone/Hydroxyapatite was studied to determine whether it changes its mechanical properties. The water contact angle and surface roughness of the compressed coated layer were also measured. The results showed a significant increase in elastic modulus, with mean values ranging from 0.464 GPa to 1.199 GPa (p<0.05). The average scratch hardness also increased significantly from 69.9 MPa to 95.7 MPa after compression, but the surface roughness and wettability decreased significantly (p<0.05). Simple compression enhanced the mechanical properties of the sulphonated poly ether ether ketone/hydroxyapatite coated layer, and the desired mechanical properties for orthopaedic and dental implant application can be achieved.
Related Concept Videos
02:17Physical Properties of Ethers
An ether molecule has a net dipole moment due to the polarity of C–O bonds. Subsequently, boiling points of ethers are lower than those of alcohols of comparable molecular weight and slightly higher than those of hydrocarbons of comparable molecular weight (Table 1).
Ethers can act as hydrogen bond acceptors, making them more water-soluble than hydrocarbons, but since ethers cannot act as hydrogen bond donors, they are much less soluble in water than alcohols. Ethers are considered...
02:29Ethers from Alcohols: Alcohol Dehydration and Williamson Ether Synthesis
Ethers can be prepared from organic compounds by various methods. Some of them are discussed below,
Preparation of Ethers by Alcohol Dehydration
In this method, in the presence of protic acids, alcohol dehydrates to produce alkenes and ethers under different conditions. For example, in the presence of sulphuric acid, dehydration of ethanol at 413 K yields ethoxyethane, whereas it yields ethene at 443 K.
02:36Crown Ethers
02:28Structure and Nomenclature of Ethers
Ethers are organic compounds with an ether functional group which is characterized by an oxygen atom connected to two — identical or different — alkyl, aryl, or vinyl groups. The C–O–C linkage in dimethyl ether — the simplest ether — has an approximately tetrahedral bond angle of 110.3 degrees. The oxygen atom is sp3- hybridized, with the C–O distance being about 140 pm.
Classification of Ethers
Based on their attached substituent...
02:23Autoxidation of Ethers to Peroxides and Hydroperoxides
02:18Ethers to Alkyl Halides: Acidic Cleavage