Synthesis of Lanthanide-Ion-Doped NaYF₄ RGB Up-Conversion Nanoparticles for Anti-Counterfeiting Application

Well-defined and mono-dispersed lanthanide-ion-doped NaYF4 up-conversion nanoparticles (UCNPs) were synthesized via thermal decomposition using lanthanide oleate as the precursor. By rational selecting the dopant pairs of the doped lanthanide ions (Y3+, Yb3+, Er3+ and Tm3+) with accurate molar ratios, three-primary-color (RGB) UCNPs which exhibited green (UCNPs-G), blue (UCNPs-B) and red (UCNPs-R) fluorescence, respectively, were prepared. The X-ray diffraction (XRD) patterns showed that the three UCNPs were purely hexagonal-phase NaYF4 crystals. Transmission electron microscopy (TEM) images revealed that the synthesized UCNPs exhibited well-defined nanosphere morphology with uniform size distribution. The average diameters were 23.95±3.35 nm for UCNPs-G, 20.63±2.59 nm for UCNPs-B, and 19.24±2.37 nm for UCNPs-R, respectively. After surface modification employing polyacrylic acid (PAA) as modifier, the obtained UCNPs were converted to be hydrophilic, which can be used as fillers to construct luminescent polymer films and luminescent ink in anti-counterfeiting application.