Dentin Bond Strength of Experimental Composites Containing Bioactive Glass: Changes During Aging for up to 1 Year
Purpose:
To investigate dentin bond strength of experimental composites based on a bis-GMA/TEG-DMA composite filled with a varying amount (0 to 40 wt%) of bioactive glass 45S5 (BG) at a total filler content of 70 wt%.
Materials And Methods:
Specimens for shear bond strength testing (diameter = 3.12 mm, height = 3 mm) were bonded to human dentin using a two-step self-etch adhesive and subjected to aging in water at 37°C for 1 week, 1 month, 3 months, 6 months, and 1 year. A total of 600 specimens were prepared (6 materials × 5 aging times × 20 specimens per experimental group). Bond strength was tested by loading specimens in a universal testing machine at a constant crosshead speed of 0.5 mm/min until fracture. Reliability analysis was performed using Weibull statistics.
Results:
Experimental composites with a low BG content (up to 5 wt%) showed dentin bond strength and reliability comparable to those of the commercial reference composite. A further increase in the BG amount diminished both bond strength and reliability. The bond strength decline was linearly dependent on the amount of BG when observed within each aging time. One-year aging in water caused no deterioration of bond strength, but diminished bond reliability. The reliability after 1-year aging was similar among all composites, including the commercial reference composite.
Conclusion:
The variation in BG amount diminished the bond strength and reliability in a dose-dependent manner.
More Related Videos
07:07Development of a Direct Pulp-capping Model for the Evaluation of Pulpal Wound Healing and Reparative Dentin Formation in Mice
Published on: January 12, 2017
11:47The Effect of Interfacial Chemical Bonding in TiO2-SiO2 Composites on Their Photocatalytic NOx Abatement Performance
Published on: July 4, 2017
Related Concept Videos
01:12Bonding and Strength of Aggregate
02:49Bond Energies and Bond Lengths
00:42Ionic Bonds
When atoms gain or lose electrons to achieve a more stable electron configuration they form ions. Ionic bonds are electrostatic attractions between ions with opposite charges. Ionic compounds are rigid and brittle when solid and may dissociate into their constituent ions in water. Covalent compounds, by contrast, remain intact unless a chemical reaction breaks them.
Opposing Charges Hold Ions Together in Ionic Compounds
Ionic bonds are reversible electrostatic interactions between ions...
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
02:43Peptide Bonds
02:45Valence Bond Theory