Stabilization and Reversal of Skyrmion Lattice in Ta/CoFeB/MgO Multilayers

Recently, magnetic skyrmion has attracted much attention due to its potential application in racetrack memory and other nanodevices. In bulk chiral magnets with non-centrosymmetric crystal structures, skyrmion lattice phase has been extensively observed. However, in film or multilayers with interfacial Dzyaloshinskii-Moriya interaction, individual skyrmion is often observed. Here, we report a short-ordered skyrmion lattice observed in [Ta(5.0 nm)/CoFeB(1.5 nm)/MgO(1.0 nm)]₁₅ multilayer in a remnant state. The structure, stabilization, and reversal of these skyrmions are discussed. Applying a slightly tilted in-plane magnetic field caused reversal of the skyrmion lattice. This reversal came from disappearance of skyrmions and nucleation of new skyrmions in the interstitial regions of the lattice. Also, we investigated how the skyrmion lattice depended on the CoFeB thickness. Our findings provide a pathway to stabilize and reverse the skyrmions in multilayers films.