Effect of anaerobic cure of self-etch adhesive on degree of conversion and shear bond strength
Melissa Phaneuf1, Asmaa Haimeur2, Rodrigo França3,4
1Dental Materials Research Lab, College of Dentistry, Faculty of Health Science, University of Manitoba, Winnipeg, MB, Canada.
Objective:
The main aim was to evaluate the effect of postponing the curing of the adhesive layer until the first layer of composite resin is applied-hereby oxygen-inhibited layer (OIL) formation and its detrimental effect on the degree of conversion (DC) of self-etch adhesives should be prevented. For this purpose, the degree of conversion and shear bond strength of four current market self-etch adhesives were evaluated, assessing the effect of curing the adhesives anaerobically and then under two different thicknesses of composite resin, and compare this to the samples cured alone and in air.
Materials And Methods:
The degrees of conversion were obtained by attenuated total reflectance-Fourier transform infrared (ATR-FTIR) spectroscopy, after the samples were prepared on a glass slide. The samples were either light-cured in air or anaerobically under a clear matrix strip alone, under 2 mm of cured composite resin or under 4 mm of cured composite resin. To determine the shear bond strength (SBS), extracted molars were halved and set in acrylic. Prefabricated cured cylinders of composite resin (TPH 3, 2.4 mm in diameter) of two different lengths are placed over the adhesives under the following conditions: light-cured conventionally (2-mm-long cylinder) and light-cured anaerobically under the uncured end of the piece of composite resin (using both 2- and 4-mm-long cylinders as separate treatments). After another incubation for 24 h at 37 °C, the samples were subjected to shearing using the Bisco Shear Bond Strength Tester.
Results:
The degree of conversion of the one-step self-etch adhesives was not statistically different when cured anaerobically under a clear matrix strip or cured anaerobically under 2 mm of composite resin. These results were greater than those cured under 4 mm. Shear bond strength between samples cured in air and anaerobically were similar under 2 mm of composite resin tubes, while those cured anaerobically under 4 mm of resin showed lower shear bond strength.
Conclusion:
When cured anaerobically, one-step self-etch adhesives show a greater degree of conversion and no significant difference in degree of conversion and shear bond strength when compared to those cured in air under the same thickness of composite resin.
Clinical Relevance:
The results obtained from DC and SBS analysis show promise in placing the uncured adhesive under the composite resin and curing both the adhesive and restoration material simultaneously.
Related Concept Videos
01:12Bonding and Strength of Aggregate
00:42Ionic Bonds
When atoms gain or lose electrons to achieve a more stable electron configuration they form ions. Ionic bonds are electrostatic attractions between ions with opposite charges. Ionic compounds are rigid and brittle when solid and may dissociate into their constituent ions in water. Covalent compounds, by contrast, remain intact unless a chemical reaction breaks them.
Opposing Charges Hold Ions Together in Ionic Compounds
Ionic bonds are reversible electrostatic interactions between ions...
02:49Bond Energies and Bond Lengths
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
02:08Gene Conversion
01:20Curing of Concrete