Nd:YAG Laser Treatment of Bioglass-coated Zirconia Surface and Its Effect on Bond Strength and Phase Transformation
Purpose:
To evaluate the morphological properties, phase transformation, and microshear bond strength of composite cement to bioglass-coated zirconia surfaces treated with Nd:YAG laser.
Materials And Methods:
Seventy-five zirconia disks were divided into five groups (n = 15). Group C received no surface treatment (control). Group S was subjected to sandblasting with 50-μm aluminum oxide particles. Group B samples were coated with bioglass 45S5. Groups BL9 and BL5 received bioglass coating and laser irradiation with 9 J/cm2 and 5 J/cm2 energy density. Morphological assessment was done using atomic force microscopy (AFM) and scanning electron microscopy (SEM). Zirconia phase transformation was assessed by XRD. Microhear bond strength testing was performed using a modified microtensile tester. The data were analyzed using the Welch test and the Games-Howell test (p < 0.05).
Results:
The sandblasted and bioglass-coated groups showed the highest bond strengths compared to other groups (p < 0.05). Group S showed the highest surface roughness and the highest frequency of cohesive failure. In all samples, the tetragonal phase decreased after surface treatment. Groups BL9 and BL5 showed some levels of tetragonal to cubic phase transformation.
Conclusion:
Bioglass coating of zirconia surfaces (using the slurry method) can increase its microshear bond strength comparable to that of sandblasting. Surface roughness of sandblasted zirconia was the highest among all methods. Irradiation of Nd:YAG laser on bioglass-coated zirconia surfaces is not effective and decreases its bond strength compared to sandblasting and bioglass coating. Increasing the Nd:YAG laser energy density cannot increase the surface roughness of bioglass-coated zirconia surfaces. Bioglass coating results in transformation of the tetragonal to the cubic phase.
Related Concept Videos
01:12Bonding and Strength of Aggregate
00:42Ionic Bonds
When atoms gain or lose electrons to achieve a more stable electron configuration they form ions. Ionic bonds are electrostatic attractions between ions with opposite charges. Ionic compounds are rigid and brittle when solid and may dissociate into their constituent ions in water. Covalent compounds, by contrast, remain intact unless a chemical reaction breaks them.
Opposing Charges Hold Ions Together in Ionic Compounds
Ionic bonds are reversible electrostatic interactions between ions...
02:49Bond Energies and Bond Lengths
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
02:31Phase Transitions
02:43Peptide Bonds