Electron Scattering via Interface Optical Phonons with High Group Velocity in Wurtzite GaN-based Quantum Well...

Here we present a detailed theoretical analysis of the interaction between electrons and optical phonons of interface and confined modes in a wurtzite AlN/GaN/AlN quantum well heterostructure based on the uniaxial dielectric continuum model. The formalism describing the interface and confined mode optical phonon dispersion relation, electron-phonon scattering rates, and average group velocity of emitted optical phonons are developed and numerically calculated. The dispersion relation of the interface phonons shows a convergence to the resonant phonon frequencies 577.8 and 832.3 cm^-1 with a steep slope around the zone center indicating a large group velocity. At the onset of interface phonon emission, the average group velocity is small due to the large contribution of interface and confined mode phonons with close-to-zero group velocity, but eventually increases up to larger values than the bulk GaN acoustic phonon velocity along the wurtzite crystal c-axis (8 nm/ps). By adjusting the GaN thickness in the double heterostructure, the average group velocity can be engineered to become larger than the velocity of acoustic phonons at a specific electron energy. This suggests that the high group velocity interface mode optical phonons can be exploited to remove heat more effectively and reduce junction temperatures in GaN-based heterostructures.