Effect of cryopreservation of teeth on the structural integrity of dentin

The autotransplantation of teeth after cryopreservation has become an increasingly viable method for whole tooth replacement. While the immediate success rates are quite high, damage introduced by cryopreservation within the dentin or enamel could be detrimental to the durability of these teeth.

to determine whether cryopreservation alters the microstructure of dentin or causes a reduction of its resistance to mechanical failures.

Third molars were obtained from young donors (18≤age≤30yrs) and subjected to a cryopreservation protocol involving storage for 10days in cryoprotectant solution at -196°C. After treatment, the mid-coronal dentin was characterized in terms of its elastic modulus, strength and fatigue behavior. Scanning electron microscopy and Raman spectroscopy were used to evaluate the microstructure and integrity of collagen after cryopreservation.

There was no significant difference in the elastic modulus or flexural strength between dentin from the cryopreserved and non-cryopreserved (control) teeth. However, the cryopreservation treatment caused a significant decrease in the fatigue strength of dentin with respect to the controls, with average reduction of nearly 20%. While there were no differences apparent in the collagen matrix or fracture surfaces between the cryopreserved and control groups, the microstructure of dentin from the cryopreserved teeth exhibited unique features and damage that appear to have caused the decrease in durability.

Autotransplantation of cryopreserved teeth may be a viable option for whole tooth restorations, but hidden damage within the dentin could render these teeth more susceptible to mechanical failures by fatigue and fracture.