Effect of Different Irrigants Applied After Post Space Preparation on Push-Out Bond Strength of a Self-Etch Resin
Hamid Jalali1, Farzaneh Farid1, Sudabeh Kulivand2
1Assistant Professor, Department of Prosthodontics, Tehran University of Medical Sciences, Tehran, Iran.
Objectives:
The aim was to investigate the effect of intracanal irrigants and agents on the bond strength of intraradicular fiber posts to dentin.
Materials And Methods:
Root canals of 72 decoronated single-rooted premolars were cleaned, shaped, and obturated with gutta-percha and AH26. The specimens were incubated at 37°C and 100% humidity for seven days. Next, the coronal 10 mm of the canals were prepared to receive size 2 D.T. Light fiber post, and the specimens were randomly allocated into six groups according to the irrigants used after post space preparation: normal saline (control group), 5.25% sodium hypochlorite (NaOCl)/15 seconds, 17% ethylenediaminetetraacetic acid (EDTA)/60 seconds, 2% chlorhexidine (CHX)/5 minutes, MTAD/5 minutes, and acid-etching/15 seconds. All canals were rinsed with normal saline and dried. Fiber posts were cemented using Panavia F2.0. After 24 hours, two mid-root slices of 1mm thickness were obtained from each specimen. Push-out bond strength test was performed in a universal testing machine at 0.5mm/minute. The maximum applied load was recorded, and the bond strength was calculated in megapascal (MPa). Data were analyzed by one-way analysis of variance (ANOVA) and Tukey's test.
Results:
The mean shear bond strengths of etched (53.21±12.11 MPa), MTAD (52.47±14.75 MPa) and EDTA (49.08±10.19 MPa) groups were significantly higher than that of the control group (39.82±10.04 MPa). The difference was marginally significant for CHX group (49.8±13.57 MPa) and not significant for NaOCl group (47.15±17.64 MPa).
Conclusions:
Etching or irrigating the root canals with MTAD or EDTA after post space preparation increases the bond strength of Panavia F2.0 to dentin.
Related Concept Videos
01:20Strength of Cement
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
01:12Bonding and Strength of Aggregate
00:42Ionic Bonds
When atoms gain or lose electrons to achieve a more stable electron configuration they form ions. Ionic bonds are electrostatic attractions between ions with opposite charges. Ionic compounds are rigid and brittle when solid and may dissociate into their constituent ions in water. Covalent compounds, by contrast, remain intact unless a chemical reaction breaks them.
Opposing Charges Hold Ions Together in Ionic Compounds
Ionic bonds are reversible electrostatic interactions between ions...
02:49Bond Energies and Bond Lengths
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
02:32Bonding in Metals