Modulatory effect of simultaneously released magnesium, strontium, and silicon ions on injectable silk hydrogels for...

Injectable silk hydrogels are ideal carriers of therapeutic agents due to their biocompatibility and low immunogenicity. Injectable silk hydrogels for bone regeneration have been previously developed but often utilize expensive biologics. In this study, we have developed an injectable silk composite incorporated with a triphasic ceramic called MSM-10 (54 Mg₂SiO₄, 36 Si₃Sr₅ and 10 MgO (wt%)) capable of simultaneously releasing magnesium, silicon, and strontium ions into its environment. These ions have been previously reported to possess therapeutic effects for bone regeneration. MSM-10 particles were incorporated into the silk hydrogels at various weight percentages [0.1 (SMH-0.1), 0.6 (SMH-0.6), 1 (SMH-1) and 2 (SMH-2)]. The effects of the released ions on the physicochemical and biological properties of the silk hydrogel were comprehensively evaluated. Increased MSM-10 loading was found to hinder the gelation kinetics of the silk hydrogel through the reduction of beta-sheet phase formation, which in turn affected the required sonication time for gelation, compressive strength, force of injection, microstructure and in vitro degradation rate. Primary human osteoblasts seeded on SMH-0.6 demonstrated increased proliferation and early alkaline phosphatase activity, as well as enhanced osteogenic gene expression compared to pure silk hydrogel and SMH-0.1. In vivo results in subcutaneous mouse models showed both decreased fibrous capsule formation and increased number of new blood vessels around the injected SMH-0.1 and SMH-0.6 implants compared to pure silk hydrogels. The results in this study indicate that the ions released from MSM-10 is able to influence the physicochemical and biological properties of silk hydrogels, and SMH-0.6 in particular shows promising properties for bone regeneration.