Study on Micro-Crack Induced Precision Severing of Quartz Glass Chips

It is difficult to cut hard and brittle quartz glass chips. Hence, a method involving micro-crack-induced severing along a non-crack microgroove-apex by controlling the loading rate is proposed. The objective is to realize the rapid and precision severing of the hardest quartz glass in chip materials. Firstly, micro-grinding was employed to machine smooth microgrooves of 398⁻565 μ m in depth; then the severing force was modelled by the microgroove shape and size; finally, the severing performance of a 4-mm thick substrate was investigated experimentally. It is shown that the crack propagation occurred at the same time from the microgroove-apex and the loading point during 0.5 ms in micro-crack-induced severing. The severing efficiency is dominated by the severing time rather than the crack propagation time. When the loading rate is less than 20⁻60 mm/min, the dynamic severing is transferred to static severing. With increasing microgroove-apex radius, the severing force decreases to the critical severing force of about 160⁻180 N in the static severing, but it increases to the critical severing force in the dynamic severing. The static severing force and time are about two times and about nine times larger than the dynamic ones, respectively, but the static severing form error of 16.3 μ m/mm and surface roughness of 19.7 nm are less. It is confirmed that the ideal static severing forces are identical to the experimental results. As a result, the static severing is controllable for the accurate and smooth separation of quartz glass chips in 4 s and less.