Formulation of a covalently bonded hydroxyapatite and poly(ether ether ketone) composite
Erik Ab Hughes1,2, Andrew Parkes3, Richard L Williams1
1School of Chemical Engineering, University of Birmingham, Birmingham, UK.
Abstract:
Spinal fusion devices can be fabricated from composites based on combining hydroxyapatite and poly(ether ether ketone) phases. These implants serve as load-bearing scaffolds for the formation of new bone tissue between adjacent vertebrae. In this work, we report a novel approach to covalently bond hydroxyapatite and poly(ether ether ketone) to produce a novel composite formulation with enhanced interfacial adhesion between phases. Compared to non-linked composites (HA_PEEK), covalently linked composites (HA_L_PEEK), loaded with 1.25 vol% hydroxyapatite, possessed a greater mean flexural strength (170 ± 5.4 vs 171.7 ± 14.8 MPa (mean ± SD)) and modulus (4.8 ± 0.2 vs 5.0 ± 0.3 GPa (mean ± SD)). Although the mechanical properties were not found to be significantly different (p > 0.05), PEEK_L_HA contained substantially larger hydroxyapatite inclusions (100-1000 µm) compared to HA_PEEK (50-200 µm), due to the inherently agglomerative nature of the covalently bonded hydroxyapatite and poly(ether ether ketone) additive. Larger inclusions would expectedly weaken the HA_L_PEEK composite; however, there is no significant difference between the flexural modulus of poly(ether ether ketone) with respect to HA_L_PEEK (p = 0.13). In addition, the flexural modulus of HA_PEEK is significantly lower compared to poly(ether ether ketone) (p = 0.03). Ultimately, covalent linking reduces hydroxyapatite particulate de-bonding from the polymeric matrix and inhibits micro-crack development, culminating in enhanced transfer of stiffness between hydroxyapatite and poly(ether ether ketone) under loading.
Related Concept Videos
01:29Covalent Bonds
01:08Covalent Bonds
When two atoms share electrons to complete their valence shells, they create a covalent bond. An atom's electronegativity—the force with which shared electrons are pulled towards an atom—determines how the electrons are shared. Molecules formed with covalent bonds can be either polar or nonpolar. Atoms with similar electronegativities form nonpolar covalent bonds; the electrons are shared equally. Atoms with different electronegativities share electrons unequally,...
02:29Ethers from Alcohols: Alcohol Dehydration and Williamson Ether Synthesis
Ethers can be prepared from organic compounds by various methods. Some of them are discussed below,
Preparation of Ethers by Alcohol Dehydration
In this method, in the presence of protic acids, alcohol dehydrates to produce alkenes and ethers under different conditions. For example, in the presence of sulphuric acid, dehydration of ethanol at 413 K yields ethoxyethane, whereas it yields ethene at 443 K.
02:36Crown Ethers
02:28Structure and Nomenclature of Ethers
Ethers are organic compounds with an ether functional group which is characterized by an oxygen atom connected to two — identical or different — alkyl, aryl, or vinyl groups. The C–O–C linkage in dimethyl ether — the simplest ether — has an approximately tetrahedral bond angle of 110.3 degrees. The oxygen atom is sp3- hybridized, with the C–O distance being about 140 pm.
Classification of Ethers
Based on their attached substituent...
02:46Covalent Bonding and Lewis Structures