Effect of Silver Nanoparticles, Zinc Oxide Nanoparticles and Titanium Dioxide Nanoparticles on Microshear Bond
Zahra Jowkar1, Nazbanoo Farpour2, Fatemeh Koohpeima2
1Department of Operative Dentistry, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Islamic Republic of Iran, Phone: +98-71-36263193,
Aim:
This study was aimed to evaluate whether antibacterial pretreatment of enamel and dentin with silver nanoparticles (SNPs), zinc oxide nanoparticles (ZNPs) and titanium dioxide nanoparticles (TNPs) has any effect on the microshear bond strength of an etch-and-rinse adhesive system.
Materials And Methods:
Eighty human third molars were randomly assigned to eight subgroups (n = 10). Enamel groups included no pretreatment (E), pretreatments with SNPs (ESNP), ZNPs (EZNP) and TNPs (ETNP) before acid etching and adhesive application. Dentinal groups included no pretreat-ment (D), pretreatments with SNPs (DSNP), ZNPs (DZNP) and TNPs (DTNP). The specimens were bonded by Adper Single Bond and polyvinyl chloride microtubes and were restored with Z250 composite. The bonded surfaces underwent microshear bond strength (uSBS) test. Data in megapascal (MPa) were analyzed with the Kruskal-Wallis test and the Mann-Whitney test (p = 0.05).
Results:
There was not a significant difference among the groups in enamel (p > 0.05). There was no significant difference between the application of three nanoparticles and the control group in dentin. However, DSNPs had a higher uSBS (25.60 ± 14.61) than that of the DZNPs and DTNPs groups (p = 0.03 and p = 0.001, respectively). Also, the mean uSBS value was lower in dentin groups compared to the respective enamel groups (p < 0.05) except for groups DSNPs and ESNPs in which no significant difference was found (p > 0.05).
Conclusion:
Pretreatment with SNPs, TNPs, and ZNPs can be suggested to achieve potent antibacterial activities without compromising the bond strength. The best result was obtained for pretreatment with SNPs compared to pretreatment with TNPs or ZNPs in dentin and enamel, albeit the differences were not significant in the enamel groups.
Clinical Significance:
Effective antibacterial treatment prior to adhesive bonding application is desirable to provide successful restoration if it would not adversely affect the bond strength of the adhesive system. Nanoparticles can be applied to meet this goal.
Related Concept Videos
01:12Bonding and Strength of Aggregate
03:14Oxidation Numbers
00:42Ionic Bonds
When atoms gain or lose electrons to achieve a more stable electron configuration they form ions. Ionic bonds are electrostatic attractions between ions with opposite charges. Ionic compounds are rigid and brittle when solid and may dissociate into their constituent ions in water. Covalent compounds, by contrast, remain intact unless a chemical reaction breaks them.
Opposing Charges Hold Ions Together in Ionic Compounds
Ionic bonds are reversible electrostatic interactions between ions...
02:49Bond Energies and Bond Lengths
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
02:43Peptide Bonds