Quantitative/qualitative analysis of adhesive-dentin interface in the presence of 10-methacryloyloxydecyl dihydrogen...

Dental adhesive provides effective retention of filling materials via adhesive-dentin hybridization. The use of co-monomers, such as 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP), is thought to be crucial for hybridization owing to their ionic-binding to calcium and co-polymerization in the polymerizable adhesives. Optimal hybridization partly depends on the mechanical properties of polymerized adhesives, which are likely to be proportional to the degree of conversion ratio. This study assessed the correlation between polymerization quality and mechanical properties at the adhesive-dentin interfaces in the presence or absence of 10-MDP. In situ Raman microspectroscopy and nanoindentation tests were used concurrently to quantify the degree of conversion ratio and dynamic mechanical properties across the adhesive-dentin interfaces. Despite the excellent diffusion and apparent higher degree of co-polymerization, 10-MDP reduced the elastic modulus of the interface. The higher viscoelastic properties of the adhesive are suggestive of poor polymerization, namely polymerization linearity related to the long carboxyl chain of 10-MDP. Such reduced mechanical integrity of hybridization could also be associated with the inhibition of nano-layering between 10-MDP and mineralized tissue in the presence of hydroxyethyl methacrylate (HEMA). This potential drawback of HEMA necessitates further qualitative/quantitative characterization of adhesive-dentin hybridization using a HEMA-free/low concentration experimental 10-MDP monomer, which theoretically possesses superior chemical bonding potential to the current HEMA-rich protocol.