[Preparation and osteogenic properties of poly ( L-lactic acid)/lecithin porous scaffolds with open pore structure]

To investigate the preparation and osteogenic properties of poly ( L-lactic acid)(PLLA)/lecithin porous scaffolds with open pore structure.

PLLA/lecithin porous scaffolds with different lecithin contents (0, 5%, 10%, 20%, 30%, 40%, 50%) were prepared by thermally induced phase separation (groups A, B, C, D, E, F, and G, respectively). Scanning electron microscopy (SEM) was used to observe the surface morphology of the scaffolds. Wide-angle X-ray diffraction (XRD) and differential scanning calorimetry (DSC) were used to detect the crystallinity of the scaffolds. The water uptake ability of the scaffolds was measured. The cell growth and viability of bone marrow mesenchymal stem cells (BMSCs) of mouse on each scaffold was assessed by cell counting kit 8 (CCK-8) method. The osteogenic differentiation ability of BMSCs on each scaffold was evaluated by alkaline phosphatase (ALP) activity. Finally, a critical-size rat calvarial bone defect model was used to evaluate the osteogenesis of the scaffolds in vivo. Micro-CT was used to reconstruct the three-dimensional model of the defect area, and the bone volume and bone mineral density were quantitatively analyzed.

SEM results showed that the lecithin could slightly reduce the pore size; when lecithin content was 50%, platelet-like structure could be observed on the scaffolds. Wide angle XRD and DSC showed that the crystallinity of scaffolds gradually decreased with the increase of lecithin content. The water uptake ability test showed that the hydrophilicity of scaffolds increased with the increase of lecithin content. CCK-8 assay showed that cell activity gradually increased with the increase of culture time. After 7 days of culture, the absorbance ( A) value of groups C, D, E, and F were significantly higher than that of groups A, B, and G ( P<0.05), but no significant difference was found among groups C, D, E, and F ( P>0.05). After 14 days of osteogenic induction, with the increase of lecithin content, there was a significant difference in ALP activity of each group. The ALP activity in groups D, E, F, and G were significantly higher than that in groups A, B, and C ( P<0.05). In vivo, the results of Micro-CT examination and bone volume and bone mineral density showed that the scaffolds with 30% lecithin had the best repairing effect.

Prepared by thermally induced phase separation, the cytocompatibility, osteogenic differentiation, and bone repair ability of the PLLA/lecithin porous scaffold is obviously better than that of pure PLLA scaffold. PLLA/lecithin porous scaffold with suitable lecithin content is a promising scaffold material for bone tissue engineering.