Production of Extracellular Matrix Fibers via Sacrificial Hollow Fiber Membrane Cell Culture
Published on: February 2, 2019
The membrane with polylactide and hyaluronic fibers for skin substitute
Ewa Stodolak-Zych1, Katarzyna Rozmus1, Ewa Dzierzkowska1
1AGH University of Science and Technology, Faculty of Materials Science and Ceramics, Krakow, Poland.
Purpose:
Skin substitutes are heterogeneous group of scaffolds (natural or synthetic) and cells. We hypothesize that nanofibers with layer composition made of polylactide (PLA) and sodium hyaluronate (HA) obtained using electrospinning method are a good matrix for cell adhesion and proliferation.
Methods:
Optimal conditions of electrospinning of PLA and HA nanofibers to create layered compositions (PLA membrane covered with HA nonwovens) were determined by modifying parameters such as the appropriate amount of solvents, polymer concentration, mixing temperature and electrospinning process conditions. By changing the parameters, it was possible to control the diameter and properties of both polymer fibers. The spinning solution were characterized by surface tension and rheology. A scanning electron microscope (SEM) was used to determine the morphology and fiber diameters: PLA and HA. Structure of the PLA/HA nonwoven was analyzed using spectroscopy (FTIR/ATR). Biocompatibility of the nonwoven with fibroblasts (ECM producers) was assessed in the in vitro conditions.
Results:
The results showed that stable conditions for the formation of submicron PLA fibers were obtained using a 13% wt. solution of the polymer, dissolved in a 3:1 mixture of DCM:DMF at 45 °C. The hyaluronic fibers were prepared from a 12% wt. solution of the polymer dissolved in a 2:1 mixture of ammonia water and ethyl alcohol. All materials were biocompatible but to a different degree.
Conclusions:
The proposed laminate scaffold was characterized by a hydrophobic-hydrophilic domain surface with a maintained fiber size of both layers. The material positively underwent biocompatibility testing in contact with fibroblasts.
Related Concept Videos
01:48Classification of Skeletal Muscle Fibers
Slow-Twitch Muscle Fibers
Slow oxidative, muscle fibers appear red due to large numbers of capillaries and high levels of...
01:19Diazonium Group Substitution: –OH and –H
02:30Stability of Substituted Cyclohexanes
The two chair conformations of cyclohexanes undergo rapid interconversion at room temperature. Both forms have identical energies and stabilities, each comprising equal amounts of the equilibrium mixture. Replacing a hydrogen atom with a functional group makes the two conformations energetically non-equivalent.
For example, in...
02:34Nucleophilic Substitution Reactions
In 1896, the German chemist Paul Walden discovered that he could interconvert pure enantiomeric (+) and (-) malic acids through a series of reactions. This conversion suggested the involvement of optical inversion during the substitution reaction. Further, in 1930, Sir Christopher Ingold described for the first time two different forms of nucleophilic substitution reactions, which are known as SN1 (nucleophilic substitution unimolecular) and SN2 (nucleophilic substitution...
00:48¹H NMR of Labile Protons: Deuterium (²H) Substitution
01:30Nucleophilic Aromatic Substitution: Addition–Elimination (SNAr)
The reaction begins with an attack of the nucleophile on the carbon that holds the leaving group. This results in the delocalization of the π electrons over the ring carbons. The resonance interaction between...