Related Experiment Video

Updated: Jan 28, 2026

Exfoliation of Egyptian Blue and Han Blue, Two Alkali Earth Copper Silicate-based Pigments
12:04

Exfoliation of Egyptian Blue and Han Blue, Two Alkali Earth Copper Silicate-based Pigments

Published on: April 24, 2014

16.5K

Six-Month Color Stability Assessment of Two Calcium Silicate-Based Cements Used in Regenerative Endodontic Procedures

Paulo J Palma1, Joana A Marques2, Rui I Falacho3

  • 1Institute of Endodontics, Faculty of Medicine, University of Coimbra, 3000-075 Coimbra, Portugal. ppalma@uc.pt.

Journal of Functional Biomaterials
|March 3, 2019
PubMed
Abstract

Keywords:
Biodentinecalcium silicate-based cementsmineral trioxide aggregateregenerative endodontic procedurestooth discoloration

More Related Videos

Guided Endodontics: Three-Dimensional Planning and Template-Aided Preparation of Endodontic Access Cavities07:14

Guided Endodontics: Three-Dimensional Planning and Template-Aided Preparation of Endodontic Access Cavities

Published on: May 24, 2022

5.1K
Evaluating the Effects of Different Polishing Methods on Color Stability of Dental Restorations in Pediatric Dentistry03:37

Evaluating the Effects of Different Polishing Methods on Color Stability of Dental Restorations in Pediatric Dentistry

Published on: June 6, 2025

421

Related Concept Videos

Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
905
Soundness of Cement01:17

Soundness of Cement

The soundness of cement refers to the ability of cement paste to retain its volume after setting. Unsound cement can lead to expansion and structural damage due to the presence of free lime, magnesia, and calcium sulfate. Free lime hydrates very slowly, expanding and causing unsoundness, which is difficult to detect because it intercrystallizes with other compounds. Magnesia also reacts with water, forming crystals that can disrupt the cement's structure. Calcium sulfate can create...
560
Assessment of Airway, Skin Color, and Use of Accessory Muscles01:30

Assessment of Airway, Skin Color, and Use of Accessory Muscles

A thorough assessment of respiratory health is paramount in clinical settings to identify and manage respiratory distress and ensure adequate oxygenation. This article elaborates on the critical aspects of respiratory evaluation, including airway assessment, skin color examination, and the observation of accessory muscle use, which are integral to effectively diagnosing and managing patients with respiratory conditions.
Introduction
The initial evaluation of a patient's respiratory system...
1.6K
Portland Cement01:21

Portland Cement

Portland cement is the essential binding ingredient in concrete, made from finely ground materials including lime, iron, silica, and alumina. Lime is derived primarily from limestone, marble, marl, seashells, and clays, which also supply iron and alumina, while silica is sourced from sand, chalk, and bauxite. Contemporary manufacturing of Portland cement is a significant source of carbon dioxide emissions, prompting research into reducing its content in concrete through alternative...
672
Fineness of Cement01:15

Fineness of Cement

The fineness of cement directly influences the rate of hydration, as the hydration begins at the surface of the cement particles. In addition to hydration, the fineness of cement is vital for various properties of concrete including workability, gypsum requirement, and long-term behavior. The fineness of cement is represented in terms of the specific surface of cement which is typically measured in square meters per kilogram, with several methods available for this determination.
Direct...
508
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...