[Effect of different surface zirconium oxide treatments on binding strength between zirconia and veneering ceramics]
Yuhong Xia1, Fei Xu2, Lei Chen2
1Department of Implant and Prosthodontics, Haizhu Square Branch, Stomatological Hospital of Southern Medical University, Guangzhou 510280, China.
Objective:
To compare the effect of three different surface zirconium oxide treatments on binding strength and fracture patterns between zirconia and veneering ceramics. Methods: A total of 40 zirconia specimens and 10 nickel-chromium alloy were divided into 5 groups (n=10 in each group): a treatment group by zirconium oxide sand-blaste (Group A), a zirconia bonded porcelain group (Group B), a hot-etching solution group (Group C), a non-treatment zirconia (Group D) and a non-treatment nickel-chromium alloy group (Group E). After all treatments, a veneering porcelain (4 mm×4 mm×2 mm) was formed onto the center of all substrate specimens by plastic coating method. Shear bond strength (SBS) test with a universal testing machine was used in each group. Scanning electron microscopy was used to observe the surface morphology of the damaged specimen interface, which was randomly selected from each group. Results: The SBS test showed that there was no significant difference in SBS results between the Group A, the Group B and the Group D (both P>0.05), and both of them were significant less than that in the group E (both P<0.05). The SBS results in the Group C were significantly higher than that in the Group D, the Group A, and the Group B (all P<0.05), but there were no significant difference compared with that in the Group E (P<0.05). Conclusion: Sand-blaste and liner application on zirconia ceramic contribute no effect to binding strength between zirconia and veneering ceramics, but hot-etching solution can increase the binding strength between zirconia and veneering ceramics.
Related Concept Videos
02:18The Equilibrium Binding Constant and Binding Strength
02:18The Equilibrium Binding Constant and Binding Strength
01:19Veneer
Other veneering techniques include plain-slicing, quarter-slicing, and rift-slicing. These...
03:14Oxidation Numbers
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
01:20Strength of Cement
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...