Iridium-Based Cubic Nanocages with 1.1-nm-Thick Walls: A Highly Efficient and Durable Electrocatalyst for Water...

We report a highly active and durable water oxidation electrocatalyst based on cubic nanocages with a composition of Ir₄₄ Pd₁₀ , together with well-defined {100} facets and porous walls of roughly 1.1 nm in thickness. Such nanocages substantially outperform all the water oxidation electrocatalysts reported in literature, with an overpotential of only 226 mV for reaching 10 mA cm^-2 _geo at a loading of Ir as low as 12.5 μg_Ir  cm^-2 on the electrode in acidic media. When benchmarked against a commercial Ir/C electrocatalyst at 250 mV of overpotential, such a nanocage-based catalyst not only shows enhancements (18.1- and 26.2-fold, respectively) in terms of mass (1.99 A mg^-1 _Ir ) and specific (3.93 mA cm^-2 _Ir ) activities, but also greatly enhanced durability. The enhancements can be attributed to a combination of multiple merits, including a high utilization efficiency of Ir atoms and an open structure beneficial to the electrochemical oxidation of Ir to the active form of IrO_x .