Mixed-Matrix Membranes Formed from Multi-Dimensional Metal-Organic Frameworks for Enhanced Gas Transport and...

Mixed-matrix membranes (MMMs) formed by incorporating metal-organic frameworks (MOFs) into polymers have a general limitation in that the MOFs are typically formed into rather simple dimensionalities (such as 1D, 2D, or 3D). Each design approach has intrinsic-albeit independent-benefits, such as network percolation (1D), access to high-aspect ratios (2D), and ease of processability (3D). However, a design strategy is needed to combine multiple dimensionalities and, thereby, access the full range of transport and compositing benefits of these high-performance materials. Herein, a facile method to form multi-dimensional HKUST-1 nanoparticles is introduced by using a modulator to tune the MOF nucleation and growth mechanism. At 30 wt % multidimensional MOF loading, the MMM shows CO₂ permeabilities of approximately 2500 Barrer, which represents a 2.5-fold increase compared to that of a pure polymer without a large loss of selectivity for CO₂ /CH₄ and CO₂ /N₂ . Additionally, almost no plasticization pressure response is observed for CO₂ up to 750 psi, suggesting an unusual stability to high activity feeds.