Ultrathin, Core-Shell Structured SiO₂ Coated Mn²⁺ -Doped Perovskite Quantum Dots for Bright White Light-Emitting...

All-inorganic semiconductor perovskite quantum dots (QDs) with outstanding optoelectronic properties have already been extensively investigated and implemented in various applications. However, great challenges exist for the fabrication of nanodevices including toxicity, fast anion-exchange reactions, and unsatisfactory stability. Here, the ultrathin, core-shell structured SiO₂ coated Mn²⁺ doped CsPbX₃ (X = Br, Cl) QDs are prepared via one facile reverse microemulsion method at room temperature. By incorporation of a multibranched capping ligand of trioctylphosphine oxide, it is found that the breakage of the CsPbMnX₃ core QDs contributed from the hydrolysis of silane could be effectively blocked. The thickness of silica shell can be well-controlled within 2 nm, which gives the CsPbMnX₃ @SiO₂ QDs a high quantum yield of 50.5% and improves thermostability and water resistance. Moreover, the mixture of CsPbBr₃ QDs with green emission and CsPbMnX₃ @SiO₂ QDs with yellow emission presents no ion exchange effect and provides white light emission. As a result, a white light-emitting diode (LED) is successfully prepared by the combination of a blue on-chip LED device and the above perovskite mixture. The as-prepared white LED displays a high luminous efficiency of 68.4 lm W^-1 and a high color-rendering index of Ra = 91, demonstrating their broad future applications in solid-state lighting fields.